NASICON-type polymer-in-ceramic composite electrolytes for lithium batteries
- 21 February 2019
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Physical Chemistry Chemical Physics
- Vol. 21 (11) , 6142-6149
Abstract
With LATP/P(EO)15LiTFSI a room temperature conductivity of 4 × 10−5 Ω−1 cm−1 is achieved for very high ceramic loading (>70 wt%) and a conductivity of approximately 10−3 Ω−1 cm−1 is found at approximately 60 °C, above the melting point of the SPE.Keywords
Funding Information
- Fondazione Cariplo (2015-0753)
- Ministero dell’Istruzione, dell’Università e della Ricerca
- Regione Lombardia (2015-0753)
This publication has 41 references indexed in Scilit:
- Electrolytes for solid-state lithium rechargeable batteries: recent advances and perspectivesChemical Society Reviews, 2011
- Phase separation and local cation coordination in PEOnLiNTf2 polymer electrolytes: Lessons from solid state NMRSolid State Ionics, 2008
- Unexpected cationic distribution in tetrahedral/octahedral sites in nominal Li1+xAlxGe2−x(PO4)3 NASICON seriesSolid State Ionics, 2007
- Dependence of Ionic Conductivity on Composition of Fast Ionic Conductors Li1+xTi2-xAlx(PO4)3, 0 ≤ x ≤ 0.7. A Parallel NMR and Electric Impedance StudyChemistry of Materials, 2002
- Enhancement of ion transport in polymer electrolytes by addition of nanoscale inorganic oxidesJournal of Power Sources, 2001
- Stoichiometric changes in lithium conducting materials based on Li1+xAlxTi2−x(PO4)3: impedance, X-ray and NMR studiesSolid State Ionics, 2000
- Effects of nanoscale SiO2 on the thermal and transport properties of solvent-free, poly(ethylene oxide) (PEO)-based polymer electrolytesSolid State Ionics, 1999
- POWDER CELL – a program for the representation and manipulation of crystal structures and calculation of the resulting X-ray powder patternsJournal of Applied Crystallography, 1996
- Ionic Conductivity of Solid Electrolytes Based on Lithium Titanium PhosphateJournal of the Electrochemical Society, 1990
- Effects of inert fillers on the mechanical and electrochemical properties of lithium salt-poly(ethylene oxide) polymer electrolytesSolid State Ionics, 1982