Remineralization effectiveness of adhesive containing amorphous calcium phosphate nanoparticles on artificial initial enamel caries in a biofilm-challenged environment

Authors:
Publisher website
Google Scholar
Abstract
Objectives Dental caries is closely associated with acid-producing bacteria, and Streptococcus mutans is one of the primary etiological agents. Bacterial accumulation and dental demineralization lead to destruction of bonding interface, thus limiting the longevity of composite. The present study investigated remineralization effectiveness of adhesive containing nanoparticles of amorphous calcium phosphate (NACP) in a stimulated oral biofilm environment. Methods The enamel blocks were immersed in demineralization solution for 72 h to imitate artificial initial carious lesion and then subjected to a Streptococcus mutans biofilm for 24 h. All the samples then underwent 4-h demineralization in brain heart infusion broth with sucrose (BHIS) and 20-h remineralization in artificial saliva (AS) for 7 days. The daily pH of BHIS after 4-h incubation, lactic acid production, colony-forming unit (CFU) count, and content of calcium (Ca) and phosphate (P) in biofilm were evaluated. Meanwhile, the remineralization effectiveness of enamel was analyzed by X-ray diffraction (XRD), surface microhardness testing, transverse microradiography (TMR) and scanning electron microscopy (SEM). Results The NACP adhesive released abundant Ca and P, achieved acid neutralization, reduced lactic acid production, and lowered CFU count (P < 0.05). Enamel treated with NACP adhesive demonstrated the best remineralization effectiveness with remineralization value of 52.29 ± 4.79% according to TMR. Better microhardness recovery of cross sections and ample mineral deposits were also observed in NACP group. Conclusions The NACP adhesive exhibited good performance in remineralizing initial enamel lesion with cariogenic biofilm. Significance The NACP adhesive is promising to be applied for the protection of bonding interface, prevention of secondary caries, and longevity prolonging of the restoration.
Funding Information
  • National Natural Science Foundation of China (81800965)
  • National Natural Science Foundation of China (81670977, 51903169)
  • Sichuan Provincial Science and Technology Support Program (2017SZ0030)
  • Research Fund of Chinese Stomatological Association (Research Fund of Chinese Stomatological Association)
  • China postdoctoral foundation (2018M643507)
  • Miaozi Project in Science and Technology Innovation Program of Sichuan Province (2019037)
  • Postdoctoral Cross Funding of Sichuan University (0040304153013)

This publication has 71 references indexed in Scilit: