Relationship between Moisture Transportation, Efflorescence and Structure Degradation in Fly Ash/Slag Geopolymer

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The relationship between moisture transportation and efflorescence in sodium hydroxide- or sodium silicate-activated fly ash/slag geopolymers was investigated. The results show that the efflorescence products are sodium carbonate hydrates, mainly composed of natron, heptahydrate, trona and sodium carbonate. The efflorescence induces compressive strength loss, water absorption increases and pore structure degradation in the geopolymer. When the curved surface of a geopolymer cylinder is covered with plastic film, the moisture transportation drives the free alkalis to the top surface to initiate efflorescence. In comparison, the efflorescence occurring on the curved surface of an uncovered geopolymer cylinder results in a more intensive alkalinity loss. For the uncovered geopolymers prepared with sodium hydroxide activator, efflorescence deposits are formed on the lower half of cylinder. A low capillary absorption capacity developed in the pore structure can only drive the moisture to the middle of cylinder, which is confronted with the drying front. More efflorescence products are formed on the upper half of the uncovered geopolymer cylinder prepared with sodium silicate activator. A relatively higher capillary absorption capacity, developed in the more compact pore structure, transports the moisture from the bottom to the top of cylinder, so no drying line is observed in the cylinder.
Funding Information
  • National Natural Science Foundation of China (51708199)
  • Guizhou Provincial Science and Technology Department (2020-4Y047; 2018-133-042)
  • the Innovative Hunan Province Special Funds of China (2019GK011)
  • Fundamental Research Funds for the Central Universities (531118010069)
  • Science and Technology Project of Transportation and Communication Ministry of Guizhou Province (2017-143-054)
  • Science and Technology Program of Beijing (Z181100003918005)

This publication has 27 references indexed in Scilit: