Designing against fracture in brittle plastics

Authors:
Publisher website
Google Scholar
Abstract
The fracture toughness of a variety of sharply notched tension, bending and rotating disc specimens of PMMA is examined using linear fracture mechanics. It is observed that rapid fracture with a brittle glassy appearance usually follows a period of slow crack growth, denoted by fan shaped markings of local ductility, though still brittle overall. In this near brittle regime the fracture toughness is sensitive to strain rate so that high values of effective surface energy are easily induced by rapid testing or notch bluntness. At impact rates the toughness increases again. For design purposes, in the absence of environmental effects, the onset of slow cracking and rapid (glassy) fracture, can be associated with fracture toughness K 1c of about 800 Ibf/in 3/2 (90 kg/cm 3/2 ) and 1600 Ibf/in 3/2 (180 kg/cm 3/2 ) respectively. Detailed studies have not been made on other materials but a guide to the levels of notch toughness and notch brittle temperatures are given for several plastics.

This publication has 8 references indexed in Scilit: