Near‐Theoretical Thermal Conductivity Silver Nanoflakes as Reinforcements in Gap‐Filling Adhesives

Authors:
Top Cited Papers
Publisher website
Google Scholar
Abstract
The rapid development of highly integrated microelectronic devices causes urgent demands for advanced thermally conductive adhesives (TCAs) to solve the interfacial heat‐transfer issue. Due to their natural 2D structure and isotropic thermal conductivity, metal nanoflakes are promising fillers blended with polymer to develop high‐performance TCAs. However, achieving corresponding TCAs with thermal conductivity over 10 W m−1 K−1 at filler content below 30 vol% remains challenging so far. This longstanding bottleneck is mainly attributed to the fact that most current metal nanoflakes are prepared by “bottom‐up” processes (e.g., solution‐based chemical synthesis) and inevitably contain lattice defects or impurities, resulting in lower intrinsic thermal conductivities, only 20–65% of the theoretical value. Here, a “top‐down” strategy by splitting highly purified Ag foil with nanoscale thickness is adopted to prepare 2D Ag nanoflakes with an intrinsic thermal conductivity of 398.2 W m−1 K−1, reaching 93% of the theoretical value. After directly blending with epoxy, the resultant Ag/epoxy exhibits a thermal conductivity of 15.1 W m−1 K−1 at low filler content of 18.6 vol%. Additionally, in practical microelectronic cooling performance evaluations, the interfacial heat‐transfer efficiency of the Ag/epoxy achieves ≈1.4 times that of the state‐of‐the‐art commercial TCA.
Funding Information
  • National Natural Science Foundation of China (52102055, 5227020331, 52075527)
  • Chinese Academy of Sciences (XDC07030100, XDA22020602, ZDKYYQ20200001, ZDRW‐CN‐2019‐3)
  • Natural Science Foundation of Ningbo Municipality (2017A610010)
  • China Postdoctoral Science Foundation (2020M681965, 2022M713243)

This publication has 74 references indexed in Scilit: