Influence of Pre-Strain on Static and Fatigue Properties of S420M Steel
Open Access
Abstract
This paper reports the results of static tensile and low-cycle fatigue tests on S420M steel specimens. As-received (unstrained) and pre-strained specimens were used during the tests. Based on the static tensile tests carried out, no effect of pre-strain on the basic strength parameters of the S420M steel was found. Low-cycle fatigue tests showed that the pre-strain of the specimens causes a change in the cyclic properties of the steel and a slight increase in fatigue life compared to that of the as-received specimens. The greatest increase in durability was observed at the lowest strain levels.Keywords
Funding Information
- Narodowe Centrum Nauki (2017/25/B/ST8/02256)
This publication has 28 references indexed in Scilit:
- Experimental investigation on the effect of tensile pre-strain on ratcheting behavior of 430 Stainless Steel under fully-reversed loading conditionEngineering Failure Analysis, 2011
- Fatigue Behavior of Stainless Steel 304L Including Strain Hardening, Prestraining, and Mean Stress EffectsJournal of Engineering Materials and Technology, 2010
- The influence of pre-straining on the high-cycle fatigue performance of two hot-dip galvanised car body steelsMaterials Characterization, 2007
- On pre-straining and the evolution of material anisotropy in sheet metalsInternational Journal of Plasticity, 2005
- On the Ohno?Wang kinematic hardening rules for multiaxial ratcheting modeling of medium carbon steelInternational Journal of Plasticity, 2005
- Cyclic stress-strain behavior of 9Cr1Mo steel at positive mean stressMaterials Science and Engineering: A, 2001
- Effect of pre-strain and mean stress on cyclic plastic deformation response of iron-based alloysMaterials Science and Engineering: A, 2001
- Effect of loading history on cyclic stress–strain responseMaterials Science and Engineering: A, 2001
- Thermal Ratcheting Criteria and Behavior of Piping ElbowsJournal of Pressure Vessel Technology, 1990
- The effect of pre-strain on fatigue crack growth and crack closureEngineering Fracture Mechanics, 1976