Anisotropic Wetting of Microstructured Surfaces as a Function of Surface Chemistry

Authors:
Publisher website
Google Scholar
Abstract
In order to study the influence of surface chemistry on the wetting of structured surfaces, microstructures consisting of grooves or squares were produced via hot embossing of poly(ethylene-alt-tetrafluoroethylene) ETFE substrates. The structured substrates were modified with polymer brushes, thereby changing their surface functionality and wettability. Water droplets were most strongly pinned to the structure when the surface was moderately hydrophilic, as in the case of poly(4-vinylpyridine) (P4VP) or poly(vinyl(N-methyl-2-pyridone) (PVMP) brush-modified substrates. As a result, the droplet shape was determined by the features of the microstructure. The water contact angles (CA) were considerably higher than on flat surfaces and differed, in the most extreme case, by 37° when measured on grooved substrates, parallel and perpendicular to the grooves. On hydrophobic substrates (pristine ETFE), the same effects were observed but were much less pronounced. On very hydrophilic sampes (those modified with poly(N-methyl-vinylpyridinium) (QP4VP)), the microstructure had no influence on the drop shape. These findings are explained by significant differences in apparent and real contact angles at the relatively smooth edges of the embossed structures. Finally, the highly anisotropic grooved microstructure was combined with a gradient in polymer brush composition and wettability. In the case of a parallel alignment of the gradient direction to the grooves, the directed spreading of water droplets could be observed.

This publication has 25 references indexed in Scilit: