Enhancing the Structural Stability and Diffusion Kinetics of a Tunnel-Phase Cathode by the Synergistic Effect of Cation-Anion Co-Doping for Advanced Sodium-Ion Batteries

Authors:
Open Access
Publisher website
Google Scholar
Abstract
Tunnel-structured Na0.44MnO2 (NMO) has been extensively studied as a potential cathode for sodium-ion batteries (SIBs) due to its favorable cycling endurance, cost-effectiveness, environmental benignity, and notable air-moisture stability. However, limitations, such as sluggish ion diffusion kinetics, an insufficient Na+ storage capacity, and an unsatisfactory Jahn–Teller effect, impede its widespread application. To address these problems, this study proposes a co-doping strategy that involves the simultaneous introduction of a cation and an anion. The optimized cathode Na0.44Mn0.99Ni0.01O1.985F0.015 demonstrates remarkable rate capabilities with average discharge capacities of 136.2, 133.0, 129.6, 124.0, 115.9, and 95.8 mAh g−1 under current rates ranging from 0.1 to 5 C. Furthermore, it also exhibits exceptional long-term cyclability, retaining 86.5% and 89.4% capacity retention at 1 and 5 C after 200 and 400 cycles, respectively, accompanied by nearly 100% Coulombic efficiency. A comprehensive structural characterization and experimental analysis reveal that the synergistic incorporation of Ni and F can effectively adjust the lattice parameters and alleviate the Jahn–Teller distortion of the NMO cathode, thereby resulting in enhanced structural integrity, rapid ion transfer dynamics, and excellent sodium storage performance. Consequently, this investigation establishes a significant approach for optimizing tunnel-phase Mn-based cathodes through the synergistic effect of cation and anion co-doping, which promotes the practical implementation of advanced SIBs.
Funding Information
  • Shandong Province Natural Science Foundation (ZR2022QB006, 318052014, 318052015)
  • Doctoral Initiation Program of Liaocheng University (ZR2022QB006, 318052014, 318052015)

This publication has 54 references indexed in Scilit: