Air‐ and Moisture Robust Surface Modification for Ni‐Rich Layered Cathode Materials for Li‐Ion Batteries

Authors:
Open Access
Publisher website
Google Scholar
Abstract
The mainstream of high‐energy cathode development is focused on increasing the Ni‐ratio in layered structured cathode materials. The increment of the Ni portion in the layered cathode material escalates not only the deliverable capacity but also the structural degradation. High‐Ni layered cathodes are highly vulnerable to exposure to air that contains CO2 and H2O, forming problematic residual lithium compounds at the surface. In this work, a novel air‐ and moisture robust surface modification is reported for LiNi0.8Co0.1Mn0.1O2 (NCM811) via the sol‐gel coating method that selectively coats the internal surface area of the polycrystalline morphology secondary particles. Bare‐, Li2SnO3‐coated and LiCoO2‐coated NCM811 are exposed to different ambient environments (air, hot‐air, and moisture‐air) to systematically investigate the correlation between the internal/external coating morphology and performance degradations. The LiCoO2‐coated NCM811s exhibit high‐capacity retention after exposure to all environments, due to the internal surface coating that prevents the penetration of harmful compounds into the polycrystalline NCM811. On the other hand, the Li2SnO3‐coated NCM811s exposed to the ambient environments show gradual capacity fading, implying the occurrence of internal degradation. This paper highlights the impact of the internal degradation of polycrystalline NCM811 after environmental exposure and the correct coating mechanisms required to successfully prevent it.
Funding Information
  • National Research Foundation of Korea (2020R1A4A1019463)
  • Korea Institute of Energy Technology Evaluation and Planning (20221B1010003B)

This publication has 34 references indexed in Scilit: