Laser-assisted low temperature processing of Pb(Zr, Ti)O3 thin film

A method for lowering the processing temperature of ${\mathrm{PbZr}}_{\text{1−x}}{\mathrm{Ti}}_x{\mathrm{O}}_{\mathrm{3}}$ (PZT) films was developed utilizing a laser-assisted two-step process. In the first step, perovskite phase was initiated in the PZT films to a furnace anneal at low temperatures in the range of 470–550 °C, depending on the Zr/Ti ratio. Later, the films were laser annealed (using KrF excimer laser) at room temperature to grow the perovskite phase, and to improve microstructure and ferroelectric properties. It was found that this two-step process was very effective in producing excellent quality ferroelectric PZT films at low temperatures. It should be noted that although laser annealing of amorphous and/or pyrochlore films directly (one-step process) produced perovskite phase, the ferroelectric properties of these films, irrespective of the composition, were rather unattractive. Some possible reasons for the ineffectiveness of the one-step process were discussed.