Design of a Laminated Ceramic Composite for Improved Strength and Toughness

Authors:
Publisher website
Google Scholar
Abstract
Adding aluminum titanate to alumina can result in dramatic improvements in toughness and R ‐curve properties. However, the improved toughness is offset by a significant reduction in strength at small flaw sizes. This problem can be overcome through the use of a laminated composite construction. By placing a thin layer of high‐strength material on the surface of a high‐toughness body, the toughness and flaw tolerance of the body material can be maintained without sacrificing small flaw strength. In this study, alumina + 20 vol% aluminum titanate (AAT20) was used for both the surface layer and the bulk material. The surface material was a homogeneous, fine‐grained mixture of the two phases, while the bulk was an inhomogeneous mixture having a bimodal grain structure. In monolithic form, the homogeneous AAT20 displays a nearly P −1/3 indentation strength response, and the inhomogeneous material displays a flat strength response, indicative of R ‐curve behavior. The trilayer material shows a composite indentation strength response, with high strength throughout the entire range of starting flaw sizes. A method for predetermining the optimum surface layer thickness is presented. The processing and mechanical properties of these materials will be discussed.

This publication has 11 references indexed in Scilit: