Both increasing the Iso-to-Col transition and lowering the solidifying temperatures of a triazine-based dendrimer by introducing CN polar groups in the dendritic core

Authors:
Publisher website
Google Scholar
Abstract
Two new triazine-based dendrimers 1a and 1b, containing –NY(CH2)3NY– linkers between two G3 dendrons (1a: Y = Bz, 1b: Y = 4-cyanoBz; Bz = benzyl), were successfully prepared in ∼32 and ∼34% yields, respectively. Compared with dendrimer 1c that contains –NH(CH2)3NH– linkers between two G3 dendrons, dendrimer 1a exhibits a similar mesogenic range to 1c, but 1b possesses a broader mesophase-temperature range than 1c. Surprisingly, dendrimer 1b not only increases the isotropic-phase-to-columnar-mesophase (Iso-to-Col) transition temperature but also lowers the solidifying temperature on cooling. It is believed that the CN groups in the dendritic linker of 1b increase both the molecular interaction between dendrimers, leading to its increasing Iso-to-Col transition temperature, and dendritic distances within columns, leading to its decreasing solidifying temperature.
Funding Information
  • National Chi Nan University
  • Ministry of Science and Technology, Taiwan (105-2119-M-260-006-MY3)

This publication has 71 references indexed in Scilit: