Bioleaching of Lizardite by Magnesium- and Nickel-Resistant Fungal Isolate from Serpentinite Soils—Implication for Carbon Capture and Storage

Authors:
Publisher website
Google Scholar
Abstract
The major goal of this study was to evaluate the potential of fungal species indigenous to mine tailing soils in accelerating Mg release from lizardite (a polymorph of serpentine) at ambient T/P conditions. We characterized the culturable fungal isolates at three sampling sites representative of different degrees of mineral weathering by isolating the genomic subunits and internal transcribed spacer (ITS) rRNA genes using PCR and sequencing of cloned fragments. We chose the specific strain primarily identified as Talaromyces sp. for the further experiments with lizardite because of this strain's remarkable tolerance to high [Mg2+] (1 mol·L−1) and [Ni2+] (10 mM·L−1) levels in the screening test and its ubiquity in the most severely weathered samples. Results of dissolution experiments revealed that both magnesium-release rate and efficiency were significantly increased (e.g., by a factor of up to 15) in the presence of fungal cells than those in the abiotic controls. The enhanced dissolution of lizardite was mainly attributed to the fungal production of organic acids including oxalic acid, gluconic acid, formic acid, and fumaric acid added to the solution. The proton-promoted dissolution, however, was indicated not to be the only mechanism for fungus-lizardite interactions as much lesser Mg (in wt.%) was recovered in the abiotic system where the solution pH was constantly adjusted to match that of the fungal system. We also explored the dependence of fungal dissolution (of lizardite) on temperature and mineral particle sizes. In particular, we found that up to ∼ 50 wt.% of Mg was released from mineral particles of ∼ 50 μm within 30 days at 38°C, ∼ 26% and 8% higher than that at 18°C and 28°C, respectively. At the same temperature of 28°C, the Mg-release efficiency increased from 12.2 wt% for particles of ∼ 270 μm to 38.4 wt% for those of ∼100 μm although no apparent difference was recognized when the particle size decreased below 100 μm. The nonlinear correlation of dissolution rates with particle surface areas suggested that the dissolution process was controlled by mineral surface-structural modification along with Mg release and by fungal cells’ interaction with these surface structures. An amorphous layer of Mg-depleted silica was detected at the reacted mineral surface by scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). Formation of glushinskite (MgC2O4·2H2O) was also observed when oxalate was accumulated to certain concentrations in the solution. Overall, this study showed that the isolated Talaromyces sp. was a promising bioagent to improve the efficacy of cation release from serpentine minerals for the purpose of carbon sequestration and resource recovery.

This publication has 48 references indexed in Scilit: