This work presents the research results on the development of an innovative, hydrometallurgical technology for the production of manganese(II) perrhenate dihydrate from recycled waste. These wastes are scraps of Ni-based superalloys containing Re and scraps of Li–ion batteries containing Mn—specifically, solutions from the leaching of black mass. This work presents the conditions for the production of Mn(ReO₄)₂·2H₂O. Thus, to obtain Mn(ReO₄)₂·2H₂O, manganese(II) oxide was used, precipitated from the solutions obtained after the leaching of black mass from Li–ion batteries scrap and purified from Cu, Fe and Al (pH = 5.2). MnO₂ precipitation was carried out at a temperature < 50 °C for 30 min using a stoichiometric amount of KMnO₄ in the presence of H₂O₂. MnO₂ precipitated in this way was purified using a 20% H₂SO₄ solution and then H₂O. Purified MnO₂ was then added alternately with a 30% H₂O₂ solution to an aqueous HReO₄ solution. The reaction was conducted at room temperature for 30 min to obtain a pH of 6–7. Mn(ReO₄)₂·2H₂O precipitated by evaporating the solution to dryness was purified by recrystallization from H₂O with the addition of H₂O₂ at least twice. Purified Mn(ReO₄)₂·2H₂O was dried at a temperature of 100–110 °C. Using the described procedure, Mn(ReO₄)₂·2H₂O was obtained with a purity of >99.0%. This technology is an example of the green transformation method, taking into account the 6R principles.

Publications with shared reference:

0 publications found