We confirmed the coverage dependent variation of tautomers of 2-mercaptothiazoline (the thiolate and thione forms) adsorbed on the Ge(100) surface under UHV conditions by using HRXPS measurements in conjunction with the DFT calculation method, which was studied before only in aqueous systems. The C 1s, S 2p, and N 1s core-level spectra obtained using HRXPS revealed the simultaneous presence of two distinct adsorption structures in different proportions at both low (0.15 ML) and high (0.65 ML) coverages. Moreover, we modelled the adsorption structures and geometric configurations of the bond states of 2-mercaptothiazoline on the Ge(100) surface by using the DFT calculation method, and found that the S dative bonded structure is the most stable adsorption structure for the thione form of 2-mercaptothiazoline and that the S–H dissociated-N dative bonded structure is the most stable adsorption structure for the thiolate form.

In this study, we selectively enhanced two types of adsorption of 3-mercaptoisobutyric acid on a Ge(100) surface by using the tunneling electrons from an STM and the catalytic effect of an STM tip. 3-Mercaptoisobutyric acid has two functional groups: a carboxylic acid group at one end of the molecule and a thiol group at the other end. It was found that the adsorption occurring through the carboxylic acid group was selectively enhanced by the application of electrons tunneling between an STM tip and the surface. Using this enhancement, it was possible to make thiol group-terminated surfaces at any desired location. In addition, via the use of a tungsten STM tip coated with a tungsten oxide (WO₃) layer, we selectively catalyzed the adsorption through the thiol group. Using this catalysis, it was possible to generate carboxylic acid group-terminated surfaces at any desired location. This functional group-selective adsorption using STM could be applied in positive lithographic methods to produce semiconductor substrates terminated by desired functional groups.

We fabricated a closely packed Au nanoparticle monolayer with millimeter dimensions on a hydrophilic Si substrate using a water/oil interface method. The surface-enhanced Raman scattering of Rhodamine 6G dye molecules adsorbed on these substrates was measured. For this structure, we simulated the electromagnetic-field enhancement when the laser light was focused on the sample, assuming the hexagonal unit cell. We suggest that the strong field enhancement arises from interstitial gaps between nanoparticles.