Kelvin G. M. Brockbank

Heart valve cryopreservation was employed as a model for the development of complex tissue preservation methods based upon vitrification and nanowarming. Porcine heart valves were loaded with cryoprotectant formulations step wise and vitrified in 1–30 mL cryoprotectant formulations ± Fe nanoparticles ± 0.6 M disaccharides, cooled to −100 °C, and stored at −135 °C. Nanowarming was performed in a single ~100 s step by inductive heating within a magnetic field. Controls consisted of fresh and convection-warmed vitrified heart valves without nanoparticles. After washing, cell viability was assessed by metabolic assay. The nanowarmed leaflets were well preserved, with a viability similar to untreated fresh leaflets over several days post warming. The convection-warmed leaflet viability was not significantly different than that of the nanowarmed leaflets immediately after rewarming; however, a significantly higher nanowarmed leaflet viability (p < 0.05) was observed over time in vitro. In contrast, the associated artery and fibrous cardiac muscle were at best 75% viable, and viability decreased over time in vitro. Supplementation of lower concentration cryoprotectant formulations with disaccharides promoted viability. Thicker tissues benefited from longer-duration cryoprotectant loading steps. The best outcomes included a post-warming incubation step with α-tocopherol and an apoptosis inhibitor, Q-VD-OPH. This work demonstrates progress in the control of ice formation and cytotoxicity hurdles for the preservation of complex tissues.

Static cold storage is the cheapest and easiest method and current gold standard to store and preserve donor organs. This study aimed to compare the preservative capacity of gluconate-lactobionate-dextran (Unisol) solutions to histidine-tryptophan-ketoglutarate (HTK) solution. Murine syngeneic heterotopic heart transplantations (Balb/c-Balb/c) were carried out after 18 h of static cold storage. Cardiac grafts were either flushed and stored with Unisol-based solutions with high-(UHK) and low-potassium (ULK) ± glutathione, or HTK. Cardiac grafts were assessed for rebeating and functionality, histomorphologic alterations, and cytokine expression. Unisol-based solutions demonstrated a faster rebeating time (UHK 56 s, UHK + Glut 44 s, ULK 45 s, ULK + Glut 47 s) compared to HTK (119.5 s) along with a better contractility early after reperfusion and at the endpoint on POD 3. Ischemic injury led to a significantly increased leukocyte recruitment, with similar degrees of tissue damage and inflammatory infiltrate in all groups, yet the number of apoptotic cells tended to be lower in ULK compared to HTK. In UHK- and ULK-treated animals, a trend toward decreased expression of proinflammatory markers was seen when compared to HTK. Unisol-based solutions showed an improved preservative capacity compared with the gold standard HTK early after cardiac transplantation. Supplemented glutathione did not further improve tissue-protective properties.

The demand for human bioengineered tissue constructs is growing in response to the worldwide movement away from the use of animals for testing of new chemicals, drug screening and household products. Presently, constructs are manufactured and delivered just in time, resulting in delays and high costs of manufacturing. Cryopreservation and banking would speed up delivery times and permit cost reduction due to larger scale manufacturing. Our objective in these studies was development of ice-free vitrification formulations and protocols using human bioengineered epithelial constructs that could be scaled up from individual constructs to 24-well plates. Initial experiments using single EpiDerm constructs in vials demonstrated viability >80% of untreated control, significantly higher than our best freezing strategy. Further studies focused on optimization and evaluation of ice-free vitrification strategies. Vitrification experiments with 55% (VS55) and 70% (VS70) cryoprotectant (CPA) formulations produced constructs with good viability shortly after rewarming, but viability decreased in the next days, post-rewarming in vitro. Protocol changes contributed to improved outcomes over time in vitro. We then transitioned from using glass vials with 1 construct to deep-well plates holding up to 24 individual constructs. Construct viability was maintained at >80% post-warming viability and >70% viability on days 1–3 in vitro. Similar viability was demonstrated for other related tissue constructs. Furthermore, we demonstrated maintenance of viability after 2–7 months of storage below −135 °C.

Application of the original vitrification protocol used for pieces of heart valves to intact heart valves has evolved over time. Ice-free cryopreservation by Protocol 1 using VS55 is limited to small samples (1–3 mL total volume) where relatively rapid cooling and warming rates are possible. VS55 cryopreservation typically provides extracellular matrix preservation with approximately 80% cell viability and tissue function compared with fresh untreated tissues. In contrast, ice-free cryopreservation using VS83, Protocols 2 and 3, permits preservation of large samples (80–100 mL total volume) with several advantages over conventional cryopreservation methods and VS55 preservation, including long-term preservation capability at −80 °C; better matrix preservation than freezing with retention of material properties; very low cell viability, reducing the risks of an immune reaction in vivo; reduced risks of microbial contamination associated with use of liquid nitrogen; improved in vivo functions; no significant recipient allogeneic immune response; simplified manufacturing process; increased operator safety because liquid nitrogen is not used; and reduced manufacturing costs. More recently, we have developed Protocol 4 in which VS55 is supplemented with sugars resulting in reduced concerns regarding nucleation during cooling and warming. This method can be used for large samples resulting in retention of cell viability and permits short-term exposure to −80 °C with long-term storage preferred at or below −135 °C.

The purpose of this study was evaluation of an ice-free cryopreservation method for heart valves in an allogeneic juvenile pulmonary sheep implant model and comparison with traditionally frozen cryopreserved valves. Hearts of 15 crossbred Whiteface sheep were procured in Minnesota. The valves were processed in South Carolina and the pulmonary valves implanted orthotopically in 12 black faced Heidschnucke sheep in Germany. The ice-free cryopreserved valves were cryopreserved in 12.6 mol/l cryoprotectant (4.65, 4.65, and 3.31 mol/l of dimethylsulfoxide, formamide and 1,2-propanediol) and stored at −80°C. Frozen valves were cryopreserved by controlled slow rate freezing in 1.4 mol/l dimethylsulfoxide and stored in vapor-phase nitrogen. Aortic valve tissues were used to evaluate the impact of preservation without implantation. Multiphoton microscopy revealed reduced but not significantly damaged extracellular matrix before implantation in frozen valves compared with ice-free tissues. Viability assessment revealed significantly less metabolic activity in the ice-free valve leaflets and artery samples compared with frozen tissues (P < 0.05). After 3 and 6 months in vivo valve function was determined by two-dimensional echo-Doppler and at 7 months the valves were explanted. Severe valvular stenosis with right heart failure was observed in recipients of frozen valves, the echo data revealed increased velocity and pressure gradients compared to ice-free valve recipients (P = 0.0403, P = 0.0591). Histo-pathology showed significantly thickened leaflets in the frozen valves (P < 0.05) and infiltrating CD3+ T-cells (P < 0.05) compared with ice-free valve leaflets. Multiphoton microscopy at explant revealed reduced inducible autofluorescence and extracellular matrix damage in the frozen explants and well preserved structures in the ice-free explant leaflets. In conclusion, ice-free cryopreservation of heart valve transplants at −80°C avoids ice formation, tissue-glass cracking and preserves extracellular matrix integrity resulting in minimal inflammation and improved hemodynamics in allogeneic juvenile sheep.