Sverre Arne Sande

The rheological changes that occur during the chemical gelation of semidilute solutions of chitosan in the presence of the low-toxicity agent glyceraldehyde (GCA) are presented and discussed in detail. The entanglement concentration for chitosan solutions was found to be approximately 0.2 wt.% and the rheological experiments were carried out on 1 wt.% chitosan solutions with various amounts of GCA at different temperatures (25 °C and 40 °C) and pH values (4.8 and 5.8). High crosslinker concentration, as well as elevated temperature and pH close to the pK_a value (pH ≈ 6.3–7) of chitosan are three parameters that all accelerate the gelation process. These conditions also promote a faster solid-like response of the gel-network in the post-gel region after long curing times. The mesh size of the gel-network after a very long (18 h) curing time was found to contract with increasing level of crosslinker addition and elevated temperature. The gelation of chitosan in the presence of other chemical crosslinker agents (glutaraldehyde and genipin) is discussed and a comparison with GCA is made. Small angle neutron scattering (SANS) results reveal structural changes between chitosan solutions, incipient gels, and mature gels.

Thermoresponsive amphiphilic biodegradable block copolymers of the type poly(ε-caprolactone-co-lactide)-poly(ethylene glycol)-poly(ε-caprolactone-co-lactide) (PCLA-PEG_m-PCLA) have great potential for various biomedical applications. In the present study, we have surveyed the effects of PEG spacer length (m = 1000 and 1500), temperature, and polymer concentration on the self-assembling process to form supramolecular structures in aqueous solutions of the PCLA-PEG_m-PCLA copolymer. This copolymer has a lower critical solution temperature, and the cloud point depends on both concentration and PEG length. Thermoreversible hydrogels are formed in the semidilute regime; the gel windows in the phase diagrams can be tuned by the concentration and length of the PEG spacer. The rheological properties of both dilute and semidilute samples were characterized; especially the sol-to-gel transition was examined. Small-angle neutron scattering (SANS) experiments reveal fundamental structural differences between the two copolymers for both dilute and semidilute samples. The intensity profiles for the copolymer with the long PEG spacer could be described by a spherical core–shell model over a broad temperature domain, whereas the copolymer with the short hydrophilic spacer forms rod-like species over an extended temperature range. This finding is supported by cryo-TEM images. At temperatures approaching macroscopic phase separation, both copolymers seem to assume extended rod-like structures.

The thermoresponsive amphiphilic block copolymer poly(d,l‐lactic acid‐co‐glycolic acid)‐block‐poly(ethylene glycol)‐block‐poly(d,l‐lactic acid‐co‐glycolic acid) (PLGA‐PEG_n‐PLGA), which exhibits a reversible temperature‐induced sol–gel transition at higher polymer concentrations in aqueous solution has attached a great deal of interest because of its potential in biomedical applications. In the present work, the length of the hydrophobic PLGA blocks is kept constant, whereas the length of the hydrophilic PEG block is altered and this variation has a pronounced impact on the phase behavior of the aqueous samples and the structure of the polymer. A short PEG block promotes gelation at a low temperature, whereas a longer PEG block shifts the gelation point to higher temperature. By using a combination of turbidity, rheology, and small angle neutron scattering (SANS) methods, the authors have revealed dramatic temperature effects. In dilute solution, the SANS experiments expose asymmetric ellipsoid structures for the copolymer with the short PEG‐spacer, whereas spherical core–shell structure is observed for the polymer with long PEG‐spacer. In the semidilute concentration regime, SANS measurements disclose similar profiles for the two copolymers. In a broad temperature interval, the transition from spherical core–shell micelles to cylindrical structure and packing of cylinders is observed. image

The aim of current study was to investigate the influence of a common non-ionic surfactant, polysorbate 80 (PS80), on radioactive labelling process of a novel PET tracer, [¹⁸F]Flutemetamol. Ferrous oxidation-xylenol orange (FOX) assay, in addition to UV/VIS and ¹H NMR spectroscopies were applied to characterise the composition of the PS80 solution after storage. Multivariate Curve Resolution (MCR) and PLS analysis was used to establish correlation between quality of the PS80 solution and the RCP obtained after labelling. The levels of unsaturated fatty acid moieties of PS80 were negatively correlated to RCP of [¹⁸F]Flutemetamol after synthesis. This explains the slight increase in RCP when stored PS80 solutions were applied in the synthesis. The mechanism behind this observation is suggested to be related to radiation induced radical formation in the unsaturated fatty acids, which subsequently causes instability of the PET tracer. UV/VIS spectroscopy was demonstrated to have the ability as a possible control tool for quality assurance of the studied radioactive labelling process. The presence of unsaturated fatty acid moieties in PS80 was found to be one of the most important factors responsible for the reduction in RCP of [¹⁸F]Flutemetamol after synthesis.