Palitha Jayaweera

Polybenzimidazole (PBI) hollow fiber membranes were used to treat flue gas desulfurization (FGD) wastewater (WW) from a coal fired power plant. Membranes were tested using both single salt solutions and real FGD WW. The PBI membranes showed >99% rejection for single salt solutions of NaCl, MgCl₂, CaSO₄, and CaCl₂ at approximately 2000 PPM (parts per million). The membranes also showed >97% rejection for FGD WW concentrations ranging from 6900 to 14,400 PPM total dissolved solids (TDS). The pH of the FGD WW was adjusted between 3.97–8.20, and there was an optimal pH between 5.31 and 7.80 where %rejection reached a maximum of >99%. The membranes were able to operate stably up to 50 °C, nearly doubling the water flux as compared to room temperature, and while maintaining >98% salt rejection.

High-performance polybenzimidazole (PBI) hollow-fiber membranes (HFMs) were fabricated through a continuous dry-jet wet spinning process at SRI International. By adjusting the spinning air gap from 4″ (10.2 cm) to 0.5″ (1.3 cm), the HFM pore sizes were enlarged dramatically without any significant change of the fiber dimensional size and barrier layer thickness. When fabricated with an air gap of 2.5″ (6.4 cm) and a surface modified by NaClO solution, the PBI HFM performance was comparable to that of a commercial reverse osmosis (RO) HFM product from Toyobo in terms of salt (NaCl) rejection and water permeability. The PBI RO HFM was positively surface charged in acidic conditions (pH < 7), which enhanced salt rejection via the Donnan effect. With an air gap of 1.5″ (3.8 cm), the PBI HFM rejected MgSO₄ and Na₂SO₄ above 95%, a result that compares favorably with that achieved by nanofiltration. In addition, the PBI HFM has a defect-free structure with an ultra-thin barrier layer and porous sublayer. We believe PBI HFMs are ideal for water purification and can be readily commercialized.

SRI International (SRI), in collaboration with Stanford University, OLI Systems (OLI), Politecnico de Milano (PoliMi), and Aqueous Systems Aps (ASApS) performed a 45-month effort to develop a promising Mixed-Salt Process (MSP) for carbon dioxide capture. The MSP combines existing ammonia and potassium-carbonate technologies with improved absorption steps for rate enhancement and ammonia emission reduction and a novel selective regeneration process with a high-pressure CO2 product to introduce a new and advanced transformational solvent-based technology. The striking advantages of the SRI MSP include: low heat of reaction, high loading of CO2, high-pressure regeneration of > 99% pure dry CO2, low sensitivity to impurities, low process cost, use of a non-degradable low-cost solvent with a very low carbon footprint for its production, low emissions, and reduced water use compared to the state-of-the-art ammonia-based and amine technologies. The overall objective of the project was to develop and test a solvent-based CO2 capture technology that can capture CO2 from existing or new pulverized coal (PC) power plants at low cost. Our specific goal was to test SRI’s newly developed MSP at the large bench-scale level to demonstrate that the process could capture CO2 at high efficiency (> 90%) with very high CO2 loading (>more » 10 wt.%), require less than 2 GJ/tonne for solvent regeneration, and produce a CO2 stream at high pressure with a purity > 95 vol.%. This 45-month MSP development program was designed to conduct (1) extensive test campaigns with different process flowsheet variants, and (2) detailed thermodynamic, kinetic, and process modeling. These tests and models were very important to identify any issues associated with the process in the early stages and then resolve them before moving into the next scale-up (> 1 MWe scale) testing. The technology development plan consisted of balanced experimental and process modeling activities as shown in Figure i. Such an approach reduces the risks associated with the process operability at large scales and provides capital and operating expenditure (CAPEX/OPEX) predictions with improved accuracies. Under the MSP development program at SRI, we performed an aggressive testing campaign with individual subsystems as well as integrated CO2 capture and regeneration system to identify the best operating conditions. The project was carried out in two budget periods (BP1 & BP2).« less

This work contributes to the design of safe and economical Generation-IV Super-Critical Water Reactors (SCWRs) by providing a basis for selecting structural materials to ensure the functionality of in-vessel components during the entire service life. During the second year of the project, we completed electrochemical characterization of the oxide film properties and investigation of crack initiation and propagation for candidate structural materials steels under supercritical conditions. We ranked candidate alloys against their susceptibility to environmentally assisted degradation based on the in situ data measure with an SRI-designed controlled distance electrochemistry (CDE) arrangement. A correlation between measurable oxide film properties and susceptibility of austenitic steels to environmentally assisted degradation was observed experimentally. One of the major practical results of the present work is the experimentally proven ability of the economical CDE technique to supply in situ data for ranking candidate structural materials for Generation-IV SCRs. A potential use of the CDE arrangement developed ar SRI for building in situ sensors monitoring water chemistry in the heat transport circuit of Generation-IV SCWRs was evaluated and proved to be feasible.