Muhammad Saleem

Cobalt-iron (CoFe) layered double hydroxides (LDHs) have received much interest for supercapacitors (SCs) because of their ion-insertable layer structure. However, there is still a need for more effort to increase their potential window and overall electrochemical energy storage capability as SC electrodes. In this work, we present a straightforward approach to synthesizing CoFe-LDHs on zinc oxide seeded carbon cloth (ZnO@CC) via a one-step hydrothermal reaction; the obtained electrode is denoted as CoFe-LDH@ZnO@CC. The electrochemical energy storage properties of CoFe-LDH@ZnO@CC are tested as an anode material using a three-electrode setup for SC applications in 1 M Na₂SO₄ electrolyte. It can operate in a wider potential window reaching up to 1.6 V, exceeding most previously reported anode materials. The CoFe-LDH@ZnO@CC displayed capacitive charge storage accounting for 76% of the total charge stored at 20 mV/s. The CoFe-LDH@ZnO@CC anode delivered a maximum capacitance of 299.8 F/g at 2 A/g, outstanding cycle stability, and retained 97.7% of the initial capacitance value for 5000 cycles at 16 A/g. This study introduces a new strategy for structurally designing electroactive materials for energy storage devices, which might be useful as an anode for SCs.

Cost-effective, clean, highly transparent, and flexible as well as a coatable packaging material is envisioned to solve or at least mitigate quality preservation issues of organic materials, originating from moisture interaction under ambient conditions. Liquid phase processing of packaging coatings using nano-clay and polyvinyl alcohol (PVOH) has been developed and reported. Detailed analysis of the developed coating revealed moisture permeability of 2.8 × 10⁻² g·cm/m²·day at 40 °C and 85% relative humidity (RH), which is in close accordance with Bharadwaj’s theoretical permeability model. Moreover, the developed coatings are not only more than 90% transparent, when exposed to white light, but also exhibit excellent flexibility and even after going through 10,000 bending cycles maintained the same blocking effect against moisture.

(1 − x)(Na_0.5Bi_0.5)TiO₃–xBi(Mg_2/3Nb_1/3)O₃ ceramics with x = 0.00 mol.% (0BMN), 0.01 mol.% (1BMN), 0.03 mol.% (3BMN), and 0.05 mol.% (5BMN) were synthesized using a solid-state processing technique. The thermogravimetric analysis (TGA) of uncalcined samples up to 730 °C showed that the maximum weight loss was observed for 3BMN, whereas the minimum weight loss was attributed to the 0BMN sample. After that, calcination was performed at 800 °C for 4 h. The XRD of calcined samples showed the successful formation of the perovskite phase with no impurity phases. 1BMN and 3BMN samples showed some of the lattice strain; however, a morphotropic phase boundary (MPB) existed around x = 0.03 between the rhombohedral and tetragonal structure. The TGA of the green pellets showed weight loss up to the sintering temperature (1100 °C) and during the 3 h holding period. 5BMN showed the maximum weight loss up to sintering temperature, as well as during the holding period, whereas 0BMN displayed the minimum weight loss up to sintering temperature, as well as some weight gain during the holding period. The relative permittivity (ε_r) was maximum at low frequencies, but the addition of BMN improved the ε_r. The frequency dependence of dielectric loss (tanδ) showed that the maximum loss was observed for 3BMN at lower frequencies, and 5BMN showed the maximum loss at higher frequency among all samples.

Au-doped ZnO–samarium nitrate (Sm) nanoparticles with fixed concentrations of Sm (1 wt %) and various concentrations of Au (0.0, 0.5, 1.0 and 1.5 wt %) were prepared and used as photoelectrodes to enhance the photovoltaic efficiency of dye-sensitized solar cells (DSSCs). The cell fabricated with 1.5 wt % of Au-doped ZnO–Sm nanoparticles film achieved an optimal efficiency of 4.35%, which is about 76% higher than that of 0.0 wt % of Au-doped ZnO–Sm-based cell (2.47%). This increase might be due to the formation of a blocking layer at the ZnO–Sm/Au interface, which inhibits the recombination of electrons. This increase may also be attributed to the addition of rare-earth ions in ZnO to enhance the non-absorbable wavelength region of light via up/down-conversion of near-infrared and ultraviolet radiations to visible emission and reduce the recombination loss of electron in the cell. The efficiency of cells may be increased by the blocking layer and up/down-conversion process and thus promote the overall performance of the cells. This work indicates that Au-doped ZnO–Sm nanoparticle films have the potential to increase the performance of DSSCs.

This paper reports on the synthesis of ZnO nanowires (NWs), as well asthe compound nanostructures of nanoparticles (NPs) and nanowires (NWs+NPs) with different coating layers of NPs on the top of NWs and their integration in dye-sensitized solar cells (DSSCs). In compound nanostructures, NWs offer direct electrical pathways for fast electron transfer, and the NPs of ZnOdispread and fill the interstices between the NWs of ZnO, offering a huge surface area for enough dye anchoring and promoting light harvesting. A significant photocurrent density of 2.64 mA/cm² and energy conversion efficiency of 1.43% was obtained with NWs-based DSSCs. The total solar-to-electric energy conversion efficiency of the NWs+a single layer of NPs was found to be 2.28%, with a short-circuit photocurrent density (J_SC) of 3.02 mA/cm², open-circuit voltage (V_OC) of 0.74 V, and a fill factor (FF) of 0.76, which is 60% higher than that of NWs cells and over 165% higher than NWs+a triple layer of NPs-based DSSCs. The improved performance was obtained due to the increased specific surface area for higher dye anchoring and light harvesting of compound nanostructures with NWs+a single layer of NPs.

Stacked layers of ZnO/TiO₂ (ZT) have prepared by sol–gel technique. Anatase phase of TiO₂ and hexagonal phase of ZnO have been obtained in all samples. Morphology of films consists of nanoparticles with an increasing grain size by increasing the number of layers. Dye-sensitized solar cells of these multilayers films have been fabricated. UV absorption spectra of dye-loaded photoanodes show that absorption of dye is increased by increasing the number of layers. The double stacked layers of ZnO/TiO₂ (ZT) show the highest efficiency of 1.36% as compared to others.