Tarek Rouissi

Industrial evolution and agricultural expansion, explained by continuing population growth, have rendered enormous problems for the world throughout the past few decades, primarily because of waste generation. To reduce environmental impact and dependence on fossil fuels, scientists have explored replacing synthetic polymers with environmentally friendly and sustainable alternatives in many emergent applications. In this regard, microbial biopolymers have gained special attention. Many biopolymers originating from various strains of bacteria, fungi, and algae have been reported and their possible applications have increased rapidly. This review focuses on the wide range of microbial biopolymers, their characteristics, and factors influencing their production. The present study also describes the environmental applications of microbial biopolymers. The use of these biopolymers is very attractive as a value-added and sustainable approach to wastewater treatment. By acting as adsorbents, coagulants, and flocculants as well as filters in membrane processes, microbial biopolymers shine as promising solutions beyond conventional methods. They can be integrated into various stages of the treatment process, further enhancing the efficiency of wastewater treatment methods. Microbial biopolymer applications in bioremediation and soil stabilization are also reviewed. Several studies have demonstrated the strong potential of biopolymers in soil improvement due to their ability to minimize permeability, eliminate heavy metals, stabilize soil, and limit erosion. Challenges related to scaling up and the downstream processing of microbial biopolymers, as well as its future perspectives in environmental applications, are also discussed.

Biochar and chitosan are considered as green and cost-effective adsorbents for water purification; the combination of these two materials may lead to an improved adsorption capacity of the generated adsorbents. Most sorption studies have been focused on the ability to adsorb one contaminant or the same type of contaminants. Thus, this study aimed to produce chitosan-biochar beads (CH-BB) and test their efficiency in the simultaneous removal of a metal-complexing antibiotic, ciprofloxacin (CIP), and three metal(loid)s (As, Cd and Pb). Modification of raw pig manure biochar resulted in an increase in its adsorption capacity, except for Pb. The highest increment was observed for As (almost 6-fold) and the lowest was observed for CIP (1.1-fold). The adsorbent was able to simultaneously remove all targeted contaminants, individually and in the mixture. The adsorption capacity of CH-BB followed the order: Pb > Cd > >As > CIP. When Pb and As were present in the same mixture, their removal efficiency increased from 0.13 ± 0.01 to 0.26 ± 0.05 mg/g for As and from 0.75 ± 0.08 to 0.85 ± 0.02 mg/g for Pb due to their co-precipitation. The CIP–metal complexation probably resulted in a reduced adsorption ability for inorganics due to the decreased concentration of free ions. The presence of metals and metalloids led to alterations in CIP’s mobility.

Recycled polylactic acid (PLAr) was reinforced with treated nanocellulosic hemp fibers for biocomposite fabrication. Cellulosic fibers were extracted from hemp fibers chemically and treated enzymatically. Treated nanocellulosic fibers (NCF) were analyzed by Fourier-transform infrared spectroscopy, X-ray diffraction, and scanning electron microscopy. Biocomposite fabrication was done with PLAr and three concentrations of treated NCF (0.1%, 0.25%, and 1% (v/v)) and then studied for thermal stability and mechanical properties. Increased thermal stability was observed with increasing NCF concentrations. The highest value for Young’s modulus was for PLAr + 0.25% (v/v) NCF (250.28 ± 5.47 MPa), which was significantly increased compared to PLAr (p = 0.022). There was a significant decrease in the tensile stress at break point for PLAr + 0.25% (v/v) NCF and PLAr + 1% (v/v) NCF as compared to control (p = 0.006 and 0.002, respectively). No significant difference was observed between treatments for tensile stress at yield.