Władysław Skoneczny

The article presents the effect of anodizing parameters of the EN AW-5251 aluminum alloy on the thickness and roughness of Al₂O₃ layers as well as their wettability and tribological properties in a sliding combination with the T7W material. The input variables were the current density of 1, 2, 3 A/dm² and the electrolyte temperature of 283, 293, 303 K. The tribological tests were performed on the T-17 tester in reciprocating motion, in conditions of technically dry friction. The tests were carried out on a 15 km road with a constant average slip speed of 0.2 m/s and a constant unit pressure of 1 MPa. The measurement of the wettability of the layers was performed using the sitting drop method, determining the contact angles on the basis of which the surface free energy was calculated. The profilographometric measurements were made. The analysis of the test results showed that the anodizing parameters significantly affect the thickness of the Al₂O₃ layers. The performed correlation analysis also showed a significant relationship between the roughness parameters and the wettability of the surface of the layers, which affects the ability to create and maintain a sliding film, which in turn translates into sliding resistance and wear of the T7W material. The analysis of friction and wear tests showed that the layer with hydrophobic properties produced at a current density of 1 A/dm² in an electrolyte at a temperature of 283 K is the most favorable for sliding associations with T7W material.

The article presents the effect of the thermo-chemical treatment of Al₂O₃ layers on their nanostructure, surface morphology, chemical composition as well as their micromechanical and sclerometric properties. Oxide layers were produced on EN AW-5251 aluminium alloy (AlMg₂) by the method of direct current anodizing in a three-component electrolyte. The thermo-chemical treatment was carried out in distilled water and aqueous solutions of Na₂SO₄·10H₂O and Na₂Cr₂O₇·2H₂O. It was shown that the thermo-chemical treatment process changes the morphology of the surface of the layers (the formation of a sub-layer from the Na₂SO₄·10H₂O and Na₂Cr₂O₇·2H₂O solutions), which directly increases the thickness of the layers by 0.37 and 1.77 µm, respectively. The thermo-chemical treatment in water also resulted in the formation of a 0.63 µm thick sub-layer. The micromechanical tests indicated a rise in the surface microhardness of the layers in the case of their thermo-chemical treatment in water and the Na₂SO₄·10H₂O solution and a decrease in the case of the layers modified in the Na₂Cr₂O₇·2H₂O solution. The highest microhardness (7.1 GPa) was exhibited by the layer modified in the Na₂SO₄·10H₂O solution. Scratch tests demonstrated that the thermo-chemically treated layers had better adhesive properties than the reference layer. The best scratch resistance was exhibited by the layer after thermo-chemical treatment in the Na₂SO₄·10H₂O solution (the highest values, practically for all the critical loads) which, together with its low roughness and high load capacity, predispose it to sliding contacts.

The article presents the effect of the anodizing parameters, as well as the thermo-chemical treatment, of Al₂O₃ layers produced on an aluminum alloy on the characterization of structure, geometrical structure of the surface (SGS), the thickness of the oxide layers, the phase composition, and their microhardness. The oxide layers were produced by the method of direct current anodizing in a three-component electrolyte. Then, thermo-chemical treatment was carried out in distilled water and aqueous solutions of sodium dichromate and sodium sulphate. The anodizing parameters and compounds for the thermo-chemical treatment were selected on the basis of Hartley’s plans. The research showed the effect of anodizing parameters on the thickness of the Al₂O₃ layers and the increase in the thickness of the layers as a result of the thermo-chemical treatment. The research showed a significant increase in the microhardness of the layers as a result of thermo-chemical treatment and its influence on the phase composition of Al₂O₃ layers. A significant influence of the thermo-chemical treatment on the geometrical structure of the surface was also found.

This article presents the influence of the anodizing parameters and thermo-chemical treatment of Al₂O₃ coatings made on aluminum alloy EN AW-5251 on the surface free energy. The oxide coating was produced by DC (Direct Current) anodizing in a ternary electrolyte. The thermo-chemical treatment of the oxide coatings was carried out using distilled water, sodium dichromate and sodium sulphate. Micrographs of the surface of the Al₂O₃ coatings were characterized using a scanning microscope (SEM). The chemical composition of the oxide coatings was identified using EDS (Energy Dispersive X-ray Spectroscopy) microanalysis. Surface free energy (SFE) calculations were performed by the Owens–Wendt method, based on wetting angle measurements made using the sessile drop technique. The highest value of surface free energy for the only anodized coatings was 46.57 mJ/m², and the lowest was 37.66 mJ/m². The contact angle measurement with glycerine was 98.06° ± 2.62°, suggesting a hydrophobic surface. The thermo-chemical treatment of the oxide coatings for most samples contributed to a significant increase in SFE, while reducing the contact angle with water. The highest value of surface free energy for the coatings after thermo-chemical treatment was 77.94 mJ/m², while the lowest was 34.98 mJ/m². Taking into account the contact angle measurement with glycerine, it was possible to obtain hydrophobic layers with the highest angle of 109.82° ± 4.79° for the sample after thermal treatment in sodium sulphate.

The article presents the influence of the anodic alumina coating nanostructure produced on aluminum alloy EN AW-5251 on the type of tribological wear process of the coating. Oxide coatings were produced electrochemically in a ternary electrolyte by the DC method. Analysis of the nanostructure of the coating was performed using ImageJ 1.50i software on micrographs taken with a scanning electron microscope (SEM). Scratch tests of the coatings were carried out using a Micron-Gamma microhardness tester. The scratch marks were subjected to surface geometric structure studies with a Form TalySurf 2 50i contact profiler. Based on the studies, it was found that changes in the manufacturing process conditions (current density, electrolyte temperature) affect changes in the coating thickness and changes in the anodic alumina coating nanostructure (quantity and diameter of nanofibers), which in turn has a significant impact on the type of tribological wear. An increase in the density of the anodizing current from 1 to 4 A/dm² causes an increase in the diameter of the nanofibers from 75.99 ± 7.7 to 124.59 ± 6.53 nm while reducing amount of fibers from 6.6 ± 0.61 to 3.8 ± 0.48 on length 1 × 10³ nm. This affects on a change in the type of tribological wear from grooving to micro-cutting.

The paper presents the influence of the surface anodizing parameters of the aluminum alloy EN AW-5251 on the physicochemical properties of the oxide layers produced on it. Micrographs of the surface of the oxide layers were taken using a scanning electron microscope (SEM). The chemical composition of cross-sections from the oxide layers was studied using energy dispersive spectroscopy (EDS). The phase structure of the Al₂O₃ layers was determined by the pattern method using X-ray diffractometry (XRD). The nanomorphology of the oxide layers were analyzed based on microscopic photographs using the ImageJ 1.50i program. The energetic state of the layers was based on the surface-free energy (SFE), calculated from measurements of contact angles using the Owens-Wendt method. The highest surface-free energy value (49.12 mJ/m²) was recorded for the sample produced at 293 K, 3 A/dm², in 60 min. The lowest surface-free energy value (31.36 mJ/m²) was recorded for the sample produced at 283 K, 1 A/dm², in 20 min (the only hydrophobic layer). The highest average value nanopore area (2358.7 nm²) was recorded for the sample produced at 303 K, 4 A/dm², in 45 min. The lowest average value nanopore area (183 nm²) was recorded for the sample produced at 313 K, 1 A/dm², in 20 min.

Nanotechnology is currently a very promising field of materials science. One of the most recent directions of research in this field is the nanotechnology of the upper layers for applications in engineering kinematic systems. The paper presents the influence of the production parameters of Al₂O₃ oxide layers on an EN AW-5251 aluminum alloy substrate on the nanostructure, nanomorphology of these layers, and their energy condition. The energy level was determined on the basis of Surface-Free Energy (SFE), determined from wettability (contact) angle measurements using the Owens-Wendt method. Using systematic scanning, the geometric structure of the surface (SGS) was determined for the produced layers. By means of a scanning electron microscope (SEM), the surface morphology and structure, and the chemical composition of the layers (EDS) were analyzed. Computer analysis of the surface nanoporosity was performed by means of the ImageJ 1.50i program. It was noted in the investigations that the oxide layer production parameters induce changes in the surface free energy of the layers. Changes in the nanomorphology of the upper layers were also observed, depending on the anodizing parameters.

It has been reported that the size and shape of the pores depend on the structure of the base metal, the type of electrolyte, and the conditions of the anodizing process. The paper presents thin Al₂O₃ oxide layer formed under hard anodizing conditions on a plate made of EN AW-5251 aluminum alloy. The oxidation of the ceramic layer was carried out for 40–80 minutes in a three-component SAS electrolyte (aqueous solution of acids: sulphuric 33 ml/l, adipic 67 g/l, and oxalic 30 g/l) at a temperature of 293–313 K, and the current density was 200–400 A/m². Presented images were taken by a scanning microscope. A computer analysis of the binary images of layers showed different shapes of pores. The structure of ceramic Al₂O₃ layers is one of the main factors determining mechanical properties. The resistance to wear of specimen-oxide coating layer depends on porosity, morphology, and roughness of the ceramic layer surface. A 3D oxide coating model, based on the computer analysis of images from a scanning electron microscope (Philips XL 30 ESEM/EDAX), was proposed.

The paper presents a one-dimensional model of heat conduction in a couple consisting of a cylinder made of a sliding plastic material, TG15, and a cuboid made of alloy AW 6061 coated with a hard anodic coating, where the couple is heated with the heat generated during friction. TG15 is a composite material based on polytetrafluoroethylene (PTFE) with a 15% graphite filler, used for piston rings in oil-free air-compressors. Measurement of temperature in the friction zone is extremely important for the understanding and analysis of the phenomena occurring therein. It is practically impossible to introduce a temperature sensor in such a place. Therefore, the interaction taking place in such a couple was modelled using numerical methods. In order to simplify and accelerate the calculations, a one-dimensional model and constant thermophysical parameters of the materials participating in friction were adopted. To solve the proposed model, the finite difference method was used (FDM). The resultant system of equations was solved by means of an explicit scheme.