Shichang Xu

The surface modification of reverse osmosis (RO) membranes to improve their anti-biofouling properties is gaining increased attention. Here, we modified the polyamide brackish water reverse osmosis (BWRO) membrane via the biomimetic co-deposition of catechol (CA)/tetraethylenepentamine (TEPA) and in situ growth of Ag nanoparticles. Ag ions were reduced into Ag nanoparticles (AgNPs) without extraneous reducing agents. The hydrophilic property of the membrane was improved, and the zeta potential was also increased after the deposition of poly (catechol/polyamine) and AgNPs. Compared with the original RO membrane, the optimized PCPA3-Ag10 membrane showed a slight reduction in water flux, and the salt rejection declined, but enhanced anti-adhesion and anti-bacterial activities were observed. The FDR_t of the PCPA3-Ag10 membranes during the filtration of BSA, SA and DTAB solution were 5.63 ± 0.09%, 18.34 ± 0.33% and 34.12 ± 0.15%, respectively, much better than those of the original membrane. Moreover, the PCPA3-Ag10 membrane exhibited a 100% reduction in the number of viable bacteria (B. subtilis and E. coli) inoculated on the membrane. The stability of the AgNPs was also high enough, and these results verify the effectiveness of poly (catechol/polyamine) and the AgNP-based modification strategy for the control of fouling.

Reverse osmosis (RO) membranes are widely used in the field of water treatment. However, there are inevitably various fouling problems during long-term use. Surface engineering of RO membranes, such as hydrophilic modification, has attracted broad attention for improving the anti-fouling performance. In this work, we constructed a green biomimetic composite modification layer on the surface of polyamide membranes using a dopamine (DA)/tannic acid (TA) co-deposited layer to bridge the polyamide surface and hydrophilic phytic acids (PhA). The DA/TA interlayer could firmly adhere to the RO membranes, reducing the aggregation of DA and providing abundant phenolic hydroxyl sites to graft PhA. Meanwhile, the anchored PhA molecule bearing six phosphate groups could effectively improve the superficial hydrophilicity. The membranes were characterized by the SEM, AFM, XPS, water contact angle test, and zeta potential test. After surface modification, the hydrophilicity, smoothness, and surface electronegativity were enhanced obviously. The flux and rejection of the virgin membrane were 76.05 L·m⁻²·h⁻¹ and 97.32%, respectively. While the modified D2/T4-PhA membrane showed decent permeability with a water flux of 57.37 L·m⁻²·h⁻¹ and a salt rejection of 98.29%. In the dynamic fouling test, the modified RO membranes demonstrated enhanced anti-fouling performance toward serum albumins (BSA), sodium alginates (SA), and dodecyl trimethyl ammonium bromides (DTAB). In addition, the modified membrane showed excellent stability in the 40 h long-term test.

In the production of acrylic acid, the concentration of acrylic acid solution from the adsorption tower was low, which would lead to significant energy consumption in the distillation process to purify acrylic acid, along with the production of a large amount of wastewater. Reverse osmosis (RO) was proposed to concentrate the acrylic acid aqueous solution taken from a specific tray in the absorption tower. The effects of operating conditions on the permeate flux and acid retention were studied with two commercial RO membranes (SWC5 and SWC6). When the operating pressure was 4 MPa and the temperature was 25 °C, the permeate fluxes of two membranes were about 20 L·m⁻²·h⁻¹. The acrylic acid and acetic acid retentions were about 80% and 78%, respectively. After being immersed in the acid solutions for several months, the characteristics of the two membranes were tested to evaluate their acid resistance. After six months of exposure to the acid solution containing 2.5% acrylic acid and 2.5% acetic acid, the retentions of acrylic acid and acetic acid were decreased by 5.7% and 4.1% for SWC5 and 4.9% and 2.2% for SWC6, respectively. The changes of membrane surface morphology and chemical composition showed the hydrolysis of some amide bonds.

In this paper, a novel piston exchanger—reciprocating-switcher energy recovery device (RS-ERD) was introduced and developed. The RS-ERD adopts the unique open/close plate design, which not only ensures a perfect sealing effect and high efficiency of the device, but also favors avoiding the destruction of micro-particles in the liquid occasionally. For proving the operating performances of the RS-ERD, an emulating RO-ERD desalination platform was established and the testing conditions were regulated as ERD capacity of 30 m³/h and operating pressure of 6.5 MPa. The experimental results indicate that the operating stability of the RS-ERD is good. The leakage ratio of the device is lower than 1.7% and the energy recovery efficiency is above 98%, which can satisfy the industrial requirements of the SWRO plant.