Yihua Sun

Nickel nanoparticles were synthesized via liquid-phase reduction of NiCl₂·6H₂O with N₂H₄·H₂O. The efficacy of different dispersing agents in preventing agglomeration was systematically compared, establishing a clear processing-dispersion correlation. Four different types of dispersants were selected to compare their effects on the microstructure and dispersibility of nano nickel powder. Among them, Ni nanoparticles prepared using sodium dodecyl sulfate (SDS) as dispersants exhibit superior microscopic morphology and dispersion. And then, the mass ratio between the precursor and dispersant was systematically optimized, resulting in spherical nickel nanoparticles with controllable particle size and favorable physical properties. When the mass ratio of SDS to Ni salt reached 150%, the prepared spherical Ni nanoparticles had the optimal dispersion and a minimum average particle size of 79 ± 12 nm. By estimating N_v, the concentration of nickel nanoparticles is about 2.15 × 10¹⁷ particles cm⁻³ at this ratio. After thermal treatment, the quality of the samples became stable beyond 415 °C with a maximum weight reduction of 6.75% at 150% SDS/Ni-salt ratio, and no residual surface sulfur was detected. The saturation magnetization of Ni nanopowders gently decreased with decreasing dispersant content from 35.3 emu·g⁻¹ to 31.6 emu·g⁻¹ at 300 K, while soft ferromagnetic behavior was maintained, which is more beneficial for the stability of multilayer ceramic capacitor performance.

High-quality BaTiO₃ nanopowders were synthesized via a sol–gel method using butyl titanate and barium serving as precursors. This study systematically investigates the influence of calcination temperature (600–1000 °C) and gel aging time (2–10 h) on the phase evolution and microstructure of the nanoparticles. A pure tetragonal phase with a high tetragonality (c/a ratio of 1.0100) and an average particle size of 140 nm was achieved at 1000 °C. X-ray photoelectron spectroscopy and Ultraviolet–Visible diffuse reflectance spectroscopy analyses revealed that high-temperature calcination induced the formation of oxygen vacancies and Ti³⁺ defects, leading to a narrowing of the optical bandgap from 3.01 eV to 2.98 eV. An optimal aging time of 4 h yielded uniform nanoparticles with a high specific surface area, whereas prolonged aging (>6 h) resulted in the re-emergence of BaCO₃ impurities and severe agglomeration due to the formation of a rigid gel network. This work provides a precise processing window for fabricating high-purity, highly tetragonal BaTiO₃ nanopowders suitable for the next generation of miniaturized electronic devices.

Innovative solar-driven heterostructure photocatalysts are promising for removing the organic contaminants in the water environment. In this work, a sequence of well-defined Z-scheme Ti-Ga co-doped ZnO/g-C₃N₄ (TGZ/CN) heterostructure photocatalysts were developed via a simple sol–gel method and the single-phase dispersion method in order to realize the cooperative improvement from the Ti/Ga co-doping and construction of heterostructure. The synthesized samples were analyzed by a variety of characterization techniques, and the photocatalytic activity was assessed by photodegradation of methylene blue (MB) under visible light irradiation. Compared to the ZnO and g-C₃N₄, the TGZ/CN composite demonstrated higher photocatalytic performance for the degradation of MB indicating an efficient photocatalytic degradation rate of 95.4% in 105 min under visible light. Moreover, the TGZ/CN photocatalyst exhibited excellent stability after five cycles of MB photodegradation. Furthermore, the as-prepared composites’ possible photocatalytic mechanism was discussed in detail. The improved photocatalytic performance primarily resulted from the effectively reduced band gap of ZnO after Ti/Ga co-doping and the facilitated separation of photoexcited e⁻/h⁺ pairs caused by the construction of Z-scheme heterojunction. This work offers novel insights in developing hybrids with highly efficient photocatalytic activity towards future environmental applications. Graphical abstract