Jason George Parsons

Water pollution from industrial dyes is a critical challenge due to the resistance of these types of compounds to degradation and potentially harmful effects on living organisms and human health. In this study, the electrochemical degradation of methylene blue (MB) was investigated using ink-based copper foam electrodes with reduced graphene oxide (rGO), antimony trioxide (Sb₂O₃), and rGO/Sb₂O₃ composites. The materials used to synthesize the electrodes were characterized by X-ray diffraction (XRD), which showed the successful synthesis of GO, rGO, and the Sb₂O₃-rGO composite. Additionally, the synthesized electrodes were examined using SEM. The MB degradation was studied using kinetic behavior and removal efficiency at pH levels from 3 through 6, monitored using UV-Vis spectroscopy. The electrocatalytic degradation was studied using sodium sulfate as the electrolyte across a pH range of 3 to 8. All electrodes investigated were determined to follow first-order kinetics. The Sb₂O₃-rGO composite showed the highest rate constants of MB degradation at pH 7 and 8, with rate constants of 0.0160 and 0.0159 min⁻¹, respectively. At the same time, the rGO ink-based electrode worked fastest at pH 3 and pH 4 with rate constants of 0.0178 and 0.0158 min⁻¹, respectively. The Sb₂O₃ also works best at pH 3 and 4 with rate constants of 0.0151 and 0.0152 min⁻¹. SEM analysis shows the composite electrode was more resilient to degradation than other materials.

The demand for effective antibacterial materials is growing rapidly in today’s world. Both metallic and metal oxide nanoparticles have been widely used as antibacterial agents against various bacterial species due to their unique mechanisms of destroying bacterial membrane cells. The current study explores the antibacterial activity of centrifugally spun fibers prepared from copper acetate polyvinylpyrrolidone (PVP) ethanol precursor solutions against both Gram-negative and Gram-positive bacteria. During the synthesis of the composite fibers, the physical and chemical conditions were optimized. The structure and morphology of the PVP/Cu-Ac fibers were analyzed using scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), and thermogravimetric analysis (TGA). The antibacterial activity of PVP/copper acetate fibers was tested against Gram-positive Staphylococcus aureus and Gram-negative Escherichia coli. The PVP/Copper acetate fibers demonstrated bactericidal activity against both bacterial strains, making the PVP/copper acetate composite fibers an effective material for biomedical applications.

In this study, a vanadyl phthalocyanine was synthesized and characterized using XRD, FTIR, and XPS, confirming the successful metalation of the phthalocyanine ring. XRD analysis showed the vanadyl phthalocyanine crystallized in the P-1 crystal lattice, with unit cell parameters a = 12.058 Å, b = 12.598 Å, and c = 8.719 Å, and the lattice angels were 96.203°, 94.941°, and 68.204°. FTIR spectroscopy supported the metalation by the disappearance of the N-H stretch of the non-metalated phthalocyanine. The vanadyl phthalocyanine was tested as a heterogenous catalyst for the conversion of fructose into methyl levulinate in H₂SO₄–methanol and HCl–methanol systems. The H₂SO₄–methanol reaction system catalyzed with the vanadyl phthalocyanine, and a zeroth-order rate constant of 1.10 × 10⁻⁶ M/s was observed, which was 1.74 times faster than sulfuric acid alone. The HCl–methanol system showed a zeroth-order of reaction with a rate constant of 2.33 × 10⁻⁶ M/s, which was 1.3 times faster than the HCl–methanol alone. While the HCl–methanol system showed a faster reaction rate, product distribution favored methyl levulinate formation in the H₂SO₄–methanol system. The main products identified were methyl levulinate and hepta-2,4-dienoic acid methyl ester, with a minor amount of hydroxymethylfurfural formed. These results suggest that vanadyl phthalocyanine can be effectively used as a catalyst to increase the rate of fructose conversion to methyl levulinate in either H₂SO₄ or HCl–methanol.

Titanium nitride and vanadium nitride–carbon-based composite systems, TiN/C and VN/C, were prepared using a new synthesis method based on the thermal decomposition of titanyl tetraphenyl porphyrin (TiOTPP) and vanadyl tetraphenyl porphyrin (VOTPP), respectively. The structure of the TiN/C and VN/C composite materials, as well as their precursors, were characterized using Fourier Transformed Infrared Spectroscopy, X-Ray diffraction (XRD), X-Ray energy dispersive (EDS) and X-Ray photoelectron spectroscopy (XPS). Morphologies of the TiN/C and VN/C composites were examined by means of scanning electron (SEM) and transmission electron (TEM) microscopy. The synthesis of the non-metalated tetraphenyl porphyrin, the titanium, and vanadium tetraphenyl porphyrin complexes were confirmed using FTIR. The thermal decomposition of the titanium and vanadium tetraphenyl porphyrin complexes produced the respective metal nitride encapsulated in a carbon matrix; this was confirmed by XRD, SEM, TEM, and XPS. From the XRD patterns, it was determined that the TiN and VN were presented in cubic form with expected space group FM-3M and 1:1 (metal:N) stoichiometry. The XPS results confirmed the presence of both TiN and VN in the carbon matrix without metal carbides. The SEM and TEM results showed that both TiN and VN nanoparticles formed small clusters throughout the carbon matrix; the EDS results revealed a uniform composition. The synthesis method presented in this work is novel and serves as an effective means to produce TiN and VN NPs with good structure and morphology embedded in a carbon matrix.

Antimony (Sb) and its composites have been recognized as potentially good anode materials for lithium-ion batteries (LIBs) due to their relatively high theoretical capacity of 660 mAh g⁻¹ and to their low cost. However, Sb-based anodes suffer from a high-volume change during the lithiation/delithiation process that results in capacity fading and anode degradation after prolonged charge/discharge cycles. To address this issue, Sb₂O₃/TiO₂ nanocomposite electrodes can be synthesized and used as anodes for LIBs with high capacity and good electrochemical stability. In the present work, TiO₂@Sb₂O₃ composites with different (TiO₂:Sb₂O₃) ratios of 0:1, 1:1, 1:4 and 3:1 were synthesized and directly used as anode materials for LIBs. The electrochemical performance of the TiO₂/Sb₂O₃ composite anode with different ratios of TiO₂ to Sb₂O₃ was evaluated by galvanostatic charge/discharge, rate performance and cyclic voltammetry. The 3:1 (TiO₂:Sb₂O₃) composite anode delivered the highest capacity compared to those of the TiO₂, SbO₃, 1:1 (TiO₂:Sb₂O₃) and 1:4 (TiO₂:Sb₂O₃) electrodes. The TiO₂@Sb₂O₃ composite anode with a 3:1 ratio exhibited a stabilized capacity of 536 mAh g⁻¹ after 100 cycles at 100 mA g⁻¹ and showed excellent rate performance, with current densities between 50 and 500 mA g⁻¹. The improved electrochemical performance was attributed to the synergistic effect of TiO₂ (i.e., the coating of Sb₂O₃ with TiO₂) on reducing the volume change of the Sb anode material after prolonged charge/discharge cycles and on maintaining a stable interface between the electrolyte and the composite electrode material.

Graphene and graphene oxide have shown good antibacterial activity against different bacterial species due to their unique physicochemical properties. Graphene oxide (GO) has been widely used to load metallic and metal oxide nanoparticles (NPs) to minimize their surface energy during processing and preparation, hence reducing their aggregation. In this work, GO was effectively synthesized and coated with different concentrations of zinc hydroxide Zn (OH)x using the precipitation method to prepare a GO/Zn (OH)x hybrid composite. The Zn (OH)x NPs and GO/Zn (OH)x nanocomposites were synthesized and characterized using various methods such as scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Coating GO with Zn (OH)x NPs resulted in improved aggregation of Zn (OH)x NPs as well as enhanced antibacterial activity of GO against Gram-positive and Gram-negative bacteria. Additionally, the effect of Zn (OH)x coating on the antibacterial properties of the GO/Zn (OH)x composite was systematically investigated. The synergistic effects of GO and Zn (OH)x NPs resulted in enhanced antibacterial properties of the composites compared to the pristine GO material. In addition, increasing the Zn (OH)x wt. % concentration led to an increased inhibition zone of the GO/Zn (H)x composite against Bacillus megaterium and E. coli bacteria.

The present work focuses on the synthesis of a vanadium nitride (VN)/carbon nanocomposite material via the thermal decomposition of vanadyl phthalocyanine (VOPC). The morphology and chemical structure of the synthesized compounds were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), Fourier transformed infrared spectroscopy (FTIR), X-ray diffraction (XRD), and X-ray photoemission spectroscopy (XPS). The successful syntheses of the VOPC and non-metalated phthalocyanine (H₂PC) precursors were confirmed using FTIR and XRD. The VN particles present a needle-like morphology in the VN synthesized by the sol-gel method. The morphology of the VN/C composite material exhibited small clusters of VN particles. The XRD analysis of the thermally decomposed VOPC indicated a mixture of amorphous carbon and VN nanoparticles (VN(TD)) with a cubic structure in the space group FM-3M consistent with that of VN. The XPS results confirmed the presence of V(III)-N bonds in the resultant material, indicating the formation of a VN/C nanocomposite. The VN/C nanocomposite synthesized through thermal decomposition exhibited a high carbon content and a cluster-like distribution of VN particles. The VN/C nanocomposite was used as an anode material in LIBs, which delivered a specific capacity of 307 mAh g⁻¹ after 100 cycles and an excellent Coulombic efficiency of 99.8 at the 100th cycle.

This work focuses on the synthesis of titanium nitride–carbon (TiN–carbon) composites by the thermal decomposition of a titanyl phthalocyanine (TiN(TD)) precursor into TiN. The synthesis of TiN was also performed using the sol-gel method (TiN(SG)) of an alkoxide/urea. The structure and morphology of the TiN–carbon and its precursors were characterized by XRD, FTIR, SEM, TEM, EDS, and XPS. The FTIR results confirmed the presence of the titanium phthalocyanine (TiOPC) complex, while the XRD data corroborated the decomposition of TiOPC into TiN. The resultant TiN exhibited a cubic structure with the FM3-M lattice, aligning with the crystal system of the synthesized TiN via the alkoxide route. The XPS results indicated that the particles synthesized from the thermal decomposition of TiOPC resulted in the formation of TiN–carbon composites. The TiN particles were present as clusters of small spherical particles within the carbon matrix, displaying a porous sponge-like morphology. The proposed thermal decomposition method resulted in the formation of metal nitride composites with high carbon content, which were used as anodes for Li-ion half cells. The TiN–carbon composite anode showed a good specific capacity after 100 cycles at a current density of 100 mAg⁻¹.

In the present study, the removal of both As(III) and As(V) from aqueous solutions using synthesized ZnO nanomaterials was achieved. The ZnO nanomaterial was synthesized using a precipitation technique and characterized using XRD, SEM, and Raman spectroscopy. XRD confirmed the ZnO nanoparticles were present in the hexagonal wurtzite structure. SEM of the particles showed they were aggregates of triangular and spherical particles. The average nanoparticle size was determined to be 62.03 ± 4.06 nm using Scherrer’s analysis of the three largest diffraction peaks. Raman spectroscopy of the ZnO nanoparticles showed only ZnO peaks, whereas the after-reaction samples indicated that As(V) was present in both As(V)- and As(III)-reacted samples. The adsorption of the ions was determined to be pH-independent, and a binding pH of 4 was selected as the pH for reaction. Batch isotherm studies showed the highest binding capacities occurred at 4 °C with 5.83 mg/g and 14.68 mg/g for As(III) and As(V), respectively. Thermodynamic studies indicated an exothermic reaction occurred and the binding of both As(III) and As(VI) took place through chemisorption, which was determined by the ΔH values of −47.29 and −63.4 kJ/mol for As(V) and As(III), respectively. In addition, the change in Gibbs free energy, ΔG, for the reaction confirmed the exothermic nature of the reaction; the spontaneity of the reaction decreased with increasing temperature. Results from batch time dependency studies showed the reaction occurred within the first 60 min of contact time.