Weiguo Yao

Unsaturated polyester resin (UPR) with excellent flame retardant is mainly obtained by adding large amounts of flame retardants, usually at the expense of mechanical properties. In this work, a reactive flame retardant containing phosphorus and nitrogen (DOPO-N) was successfully synthesized and incorporated in UPR as a crosslinker. The mechanical and flame-retardant properties of UPR composites were enhanced. UPR/30DOPO-N passed a UL-94 V-1 rating with a limiting oxygen index (LOI) of 30.8%. The tensile strength of UPR/30DOPO-N increased by 24.4%. On this basis, a small amount of modified HNTs (VHNTs) was added to further improve the flame-retardant properties of the composite. With the introduction of 3 wt% VHNTs, the composite passed the UL-94 V-0 rating. The peak of heat release rate (PHRR) and total heat release (THR) of it decreased by 60.7% and 48.3%, respectively. Moreover, the detailed flame-retarding mechanism of DOPO-N and VHNTs was investigated by thermogravimetric infrared spectroscopy (TG-IR), Raman spectra, and X-ray photoelectron spectroscopy (XPS). It was found that DOPO-N played a role in quenching the flame in the gas phase and cooperated with VHNTs to enhance the barrier effect in the condensed phase.

Dual-component epoxy resins are widely used for bonding different materials in automotive interior processing. However, due to the complexity and variability of automotive interior parts, uneven temperature distribution on curved surfaces during the thermoforming process can lead to uneven thermal stress distribution, damaging the interior components. This study focuses on addressing the damage issues caused by uneven thermal stress distribution during the thermoforming of automotive interior components. By monitoring the temperature and strain on the adhesive surface of the interior components during processing, using sensors and combining the readings with a finite element simulation, damage to the adhesive during processing was simulated. Based on this, a segmented thermoforming method for the model surface was employed, but it was found that this method did not significantly reduce the level of damage to the adhesive during application. Building upon the segmented simulation, significant results were achieved by applying temperature modulation at a certain frequency to adjust the damage of the interior components during processing. The techniques used in this study successfully reduced the unevenness of the adhesive surface temperature, improved the performance of the adhesive during application through segmented optimization and the application of ultrasound-assisted techniques, and markedly reduced the manufacturing process’s energy consumption.

In this work, a novel P/N flame-retardant monomer (PDHAA) was synthesized through reacting phenyl dichlorophosphate (PDCP) with N-hydroxyethyl acrylamide (HEAA). The structure of PDHAA was confirmed using Fourier transform infrared (FTIR) spectroscopy and proton nuclear magnetic resonance (NMR) spectroscopy. PDHAA monomer and 2-hydroxyethyl methacrylate phosphate (PM-2) monomer were mixed at different mass ratios, to prepare UV-curable coatings, and then applied to the surface of fiber needled felts (FNFs), to improve their flame retardancy. PM-2 was introduced to reduce the curing time of the flame-retardant coatings and improve the adhesion between the coating and the fiber needled felts (FNFs). The research results indicated that the surface flame-retardant FNFs had a high limiting oxygen index (LOI) and rapidly self-extinguished in a horizontal combustion test and passed a UL-94 V-0 test. At the same time, the CO and CO₂ emissions were greatly reduced, and the carbon residue rate was increased. In addition, the introduction of the coating improved the mechanical properties of the FNFs. Therefore, this simple and efficient UV-curable surface flame-retardant strategy has broad application prospects in the field of fire protection.

A relatively static and unique bubble template is successfully realized on a microporous substrate by controlling the surface tensions of the electrodeposit solution, and a nickel layer containing macropores is prepared using this bubble template. When the surface tension of the solution is 50.2 mN/m, the desired bubble template can be formed, there are fewer bubbles attached to other areas on the substrate, and a good nickel layer is obtained. In the analysis of the macropore formation process, it is found that the size of the bell-mouthed macropores can be tailored by changing the solution stirring speed or the current density to adjust the growth rate of the bubble template. The size change of a macropore is measured by the profile angle of the longitudinal macropore, section. As the solution stirring speed increases from 160 to 480 r/min, the angle range of the bell-mouthed macropores cross-sectional profile is increased from 21.0° to 44.3°. In addition, the angle range of the bell-mouthed macropore cross-sectional profile is increased from 39.3° to 46.3° with the current density increasing from 1 to 2.5 A/dm². Different from the dynamic hydrogen bubble template, the bubble template implemented in this paper stays attached on the deposition and grows slowly, which is novel and interesting, and the nickel layer containing macropores prepared using this bubble template is applied in completely different fields.