Bowen Wang

Aiming at handling the contradiction between power constraint of on-orbit manufacturing and the high energy input requirement of metal additive manufacturing (AM), this paper presents an AM process based on small-power metal fine wire feed, which produces thin-wall structures of height-to-width ratio up to 40 with core-forming power only about 50 W. In this process, thermal resistance was introduced to optimize the gradient parameters which greatly reduces the step effect of the typical AM process, succeeded in the surface roughness (Ra) less than 5 μm, comparable with that obtained by selective laser melting (SLM). After a 10 min electrolyte-plasma process, the roughness of the fabricated specimen was further reduced to 0.4 μm, without defects such as pores and cracks observed. The ultimate tensile strength of the specimens measured about 500 MPa, the relative density was 99.37, and the Vickers hardness was homogeneous. The results show that the proposed laser-Joule wire feed-direct metal deposition process (LJWF-DMD) is a very attractive solution for metal AM of high surface quality parts, particularly suitable for rapid prototyping for on-orbit AM in space.

This study investigated the anisotropic characteristics of the microstructural, mechanical and corrosion properties of CoCrFeMnNi high-entropy alloy produced by selective laser melting (SLM) additive manufacturing (AM). Under the extremely high thermal gradient during the SLM process, a columnar solidification structure with a single face-centered cubic (FCC) phase structure was formed. The crystal structure exhibited a regular checkerboard structure in the XOY plane (perpendicular to the building direction), which was composed of {110} direction and a small amount of {100} fiber texture. The cellular-dendritic sub-structures formed in the columnar crystal structure with sizes of about 500 nm in diameter. As for the mechanical properties, the XOY plane exhibited higher ultimate tensile strength and yield strength (σ_0.2) but lower elongation to failure compared to the XOZ plane (parallel to building direction), which reflected the anisotropy of the microstructure. The electrochemical test results of the different planes showed that the XOZ plane exhibited better corrosion resistance in comparison with the XOY plane in the 3.5 wt % NaCl solution, which was on account of the selective attack at the Mn-rich inter-cellular regions and the different structures of the cellular-dendritic sub-structures on different planes.

Purpose: This paper aimed to propose a novel fused-coating-based additive manufacturing (FCAM); the study of key process parameters and mechanical tests are performed to determine the proper parameters when building metal components. Design/methodology/approach: Sn63Pb37 alloy is deposited in an induction heating furnace with a fused-coating nozzle to build metal parts on a copper-clad substrate. The process parameters including nozzle pressure, nozzle and substrate temperature and nozzle gap between substrate are analyzed and found to have great influence on parts quality. The mechanical property tests between the fused-coating and casting parts are performed in horizontal and vertical directions. Also, the optical microscopy images are used to ascertain under which conditions good bonding can be achieved. Findings: A FCAM method is proposed, and the exploration study about the manufacturing process is carried out. The critical parameters are analyzed, and microscopy images prove the suitable temperature range that requires to fabricate metal parts. The mechanical tests confirm that tensile strength of printing parts is improved by 20.4 and 11.9 per cent in horizontal and vertical direction than casting parts. The experimental results indicate that there is a close relationship between process parameters and mechanical properties. Originality/value: This paper proves that FCAM provides an alternative way to quickly make functional metal parts with good quality and flexibility compared with other additive manufacturing methods. Moreover, good mechanical property is achieved than conventional casting parts.