(AlTiV)_100−xCr_x high-entropy alloys (HEAs) is expected to solve the problem of poor corrosion-wear resistance of lightweight alloys. To elucidate its corrosion-wear mechanism, three (AlTiV)_100−xCr_x alloys were prepared by vacuum arc melting method by repeating the melting five times at 240 A current.and their microstructures, mechanics, corrosion, wear, and corrosion-wear behaviors were investigated. The results indicate that (AlTiV)_100−xCr_x is a single-phase with BCC structure and the VEC of Cr5, Cr10 and Cr15 were 4.0, 4.1 and 4.2 respectively. Their hardness increase and toughness and corrosion resistance decrease with the increase of Cr content (Cr5:537.5 HV_0.2/6.7%/1.86 × 10⁻⁸ A/cm²; Cr10:572.3 HV_0.2/5.6%/2.09 × 10⁸ A/cm²; Cr15:617.6 HV_0.2/3.8%/2.51 × 10⁻⁸ A/cm²). The wear volume and the corrosion-wear volume of AlTiVCr alloys are mainly caused by the abrasive wear. However, the fatigue wear of AlTiVCr alloys could be exacerbated by a decrease in material’s toughness, corrosion resistance, and an increase in solution corrosivity. Therefore, Cr10 presents the optimal wear resistance in the deionized water, while the optimal corrosion-wear resistance in the 3.5 wt.% NaCl solution is presented by Cr5. Compared to TC4, the wear and corrosion-wear resistance were improved by 56.4% and 65.5%, respectively.

Increasingly, oil spills and industrial discharges are wreaking havoc on the water environment; in order to efficiently separate oil and water from sewage containing oil or organic solvents, a novel porous polymer (P(EHA-co-BA)) was prepared by Pickering high internal phase emulsion (HIPE) template method. To obtain polyHIPE with better oil/water separation capacities, octadecyltrichlorosilane (OTS)-modified carbon nanotubes (CNTs) and surfactants were used as costabilizers for HIPE, which improved the stability of HIPE as well as the mechanical properties and the separation efficiency of polyHIPE. In the presence of 1 wt % OTS-CNT adding in the oil phase, 1%OTS-CNT polyHIPE has high porosity (92.21%), favorable hydrophobicity (a water contact angle of 128°), and excellent mechanical properties. As a result, 1%OTS-CNT polyHIPE has high absorption of oils and oily solvents, e.g., dichloromethane up to 36 g/g, and maintains an absorption efficiency of >97% after 20 reapplications. In the formulation of polyHIPE, cinnamaldehyde (CA) has been added to provide superior antibacterial properties against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). It appears that the novel polyHIPE proposed in this work is a reusable antibacterial porous polymer with promising applications for oil-water separation.