Janos B. Nagy

ZSM-5 zeolites with varying aluminum content were subjected to steam treatments of different severities by adjusting the temperature, duration, and water vapor pressure. The steamed samples were characterized using a range of analytical techniques. A quantitative assessment of the aluminum species—namely, tetrahedrally coordinated framework Al, dislodged framework Al, non-framework pentacoordinated Al, and non-framework hexacoordinated Al—was achieved through a combination of EDX analysis on Cs-exchanged materials and quantitative ²⁷Al MAS NMR spectroscopy, including spectral simulation. Contrary to previous reports, the catalytic activity per framework Al site in unsteamed ZSM-5 increases with aluminum content at low Si/Al ratios, aligning with recently proposed medium effects. Notably, at the point of maximum activity enhancement due to steaming, equivalent amounts (1:1) of framework and dislodged framework Al—both in tetrahedral coordination—are observed. The maximum enhancement factor per framework Al site, for a given material and reaction, remains independent of the specific steaming conditions (temperature, time, and pressure). However, the degree of activity enhancement varies with the type of reaction: it is more pronounced for n-hexane cracking (α-test) than for m-xylene isomerization. This suggests that both catalyst modification and reaction characteristics contribute to the observed steam-induced activity enhancement. A synergistic interaction between Brønsted and Lewis acid sites appears to underpin these effects. One plausible mechanism involves the strengthening of Brønsted acidity in the presence of adjacent Lewis acid sites. This enhancement is expected to be more significant for n-hexane cracking, which demands higher acid strength compared to m-xylene isomerization. In cases of n-hexane cracking, the increased acid strength and the formation of olefins via reactions on Lewis acid sites may act cooperatively. Importantly, the dislodged framework Al species—tetrahedrally coordinated in the hydrated catalyst at ambient temperature and functioning as Lewis acid sites in the dehydrated zeolite under reaction conditions—are directly responsible for the observed enhancement in acid activity. The transformation of framework Al into dislodged framework Al species is reversible, as demonstrated by hydrothermal treatment of the steamed samples at 150–200 °C. Nonetheless, reinsertion of Al into the framework is not fully quantitative: a portion of the dislodged framework Al is irreversibly converted into non-framework penta- and hexacoordinated species during the hydrothermal process. Among these, non-framework pentacoordinate Al species may serve as counterions to balance the lattice charges associated with framework Al.

The primary aim of this research was to identify the optimal experimental conditions for obtaining aligned carbon nanotubes, temporarily leaving aside aspects such as the purity of carbon nanotubes, which is nonetheless crucial for potential applications in the field of nanoelectronics. The predefined alignment of CNTs can significantly influence the performance and efficiency of electronic components. In this study, two different catalytic supports based on cobalt nanoparticles, Co/SiO₂/Si and Co/C, have been utilized and compared in the catalytic chemical vapor deposition (CCVD) synthesis of CNTs. Various parameters have been examined, including the nature and thickness of the catalyst, the reaction temperature, and the pressure of the acetylene mixture entering the reactor. The results indicate that the optimal temperature for the Co/SiO₂/Si catalyst is 800 °C, while for the Co/C catalyst, it is 450 °C. The optimal Co layer thickness should be between 20 and 30 Å. CNT growth occurs from the top in the Co/C system, whereas bottom-up growth is characteristic of the Co/SiO₂/Si catalyst, making the latter more suitable for the synthesis of CNTs intended for nanoelectronic devices.

The aim of this work was to obtain cobalt nanoparticles through a physical method, which could be formed simultaneously during the Catalytic Chemical Vapour Deposition (CCVD) synthesis of carbon nanotubes, under conditions suitable for both carbon nanotube synthesis and Co-nanoparticle formation. Co nanoparticles were prepared by Physical Vapour Deposition (PVD) using a 0.05 m³ magnetron on two different substrates, SiO₂/Si and C, followed by a reduction treatment in an H₂ atmosphere. Transmission Electron Microscopy (TEM) and Field Enhanced Scanning Electron Microscopy (FE-SEM) were used to characterize the Co nanoparticles. On the SiO₂/Si substrate, cobalt silicate is formed, which stabilizes the Co nanoparticles, while the nanoparticles obtained on the C-substrate are sometimes surrounded by a layer of Co₃O₄, which deactivates the cobalt nanoparticles. To obtain suitable Co nanoparticles for carbon nanotube synthesis, the optimal Co-layer thickness is between 20 and 30 Å, and the optimal reduction temperature is 800 °C and 450 °C for SiO₂/Si and C substrates, respectively.

This article simply aims to compare two case studies concerning the purification, using carbon nanotubes, of water contaminated by the following two different common pollutants: benzoic acid and diesel. In particular, the aim is to highlight how the different natures of both of the polluting molecules and the carbon nanotubes play a fundamental role in water treatment. These two pollutants were taken into consideration because of their different chemical natures: benzoic acid is a polar pollutant, while the molecules present in diesel are substantially nonpolar. The carbon nanotubes used were both functionalized and nonfunctionalized. Functionalization is a process that allows for the introduction of functional groups onto the surface of carbon nanotubes. In this research, carboxylic functionalization was performed, which allowed for the insertion of carboxylic groups through attacks with sulfuric and nitric acids. Thanks to the results obtained, it was possible to quantify the optimization of the purification process depending on the types of carbon nanotubes and polluting molecules considered. The functionalized nanotubes exhibited greater performances in the treatment of water contaminated by benzoic acid compared to the nonfunctionalized ones. Instead, in the treatment of water contaminated by diesel, a greater purification capacity was shown by the nonfunctionalized carbon nanotubes compared to the functionalized ones.

Following the well-known pandemic, declared on 30 January 2020 by the World Health Organization, the request for new global strategies for the prevention and mitigation of the spread of the infection has come to the attention of the scientific community. Nanotechnology has often managed to provide solutions, effective responses, and valid strategies to support the fight against SARS-CoV-2. This work reports a collection of information on nanomaterials that have been used to counter the spread of the SARS-CoV-2 virus. In particular, the objective of this work was to illustrate the strategies that have made it possible to use the particular properties of nanomaterials, for the production of personal protective equipment (DIP) for the defense against the SARS-CoV-2 virus.

Following the well-known pandemic, declared on 30 January 2020 by the World Health Organi-zation, the request for new global strategies for the prevention and mitigation of the spread of the infection has come to the attention of the scientific community. Nanotechnology has often managed to provide solutions, effective responses, and valid strategies to support the fight against SARS-CoV-2. This work reports a collection of information on nanomaterials that have been used to counter the spread of the SARS-CoV-2 virus. In particular, the objective of this work is to illustrate the strategies that have made it possible to use the particular properties of nanomaterials, for the production of personal protective equipment (DIP) for the defense against the SARS-CoV-2 virus.

The purpose of this research was to evaluate the adsorbent properties of carbon nanotubes by investigating, in particular, the possibility of their use in the purification of water contaminated with automotive diesel, caused, in most cases, as a result of spillage from underground tanks, leaks from pipelines, traffic accidents, etc. In particular, we investigated whether the high molecular weights of the hydrocarbon molecules present in diesel could influence the adsorption capacity of carbon nanotubes. Initial systems consisting of water and diesel were treated with different amounts of carbon nanotubes. The final post-adsorption phases were characterized using NMR analysis, FT-IR spectroscopy and TG-DTG-DTA thermal analysis. Carbon nanotubes showed great efficiency in the adsorption of diesel, the possibility of their reuse in several adsorption cycles and the consequent recovery of the adsorbed diesel and of the treated water.

In this work, the possibility of using carbon nanotubes for the treatment of olive vegetation waters (OVWs) was investigated. In general, the disposal of OVWs represents an important environmental problem. The possibility of considering these waters no longer just as a problem but as a source of noble substances, thanks to the recovery of biophenols from them, was tested. In particular, predetermined quantities of olive vegetation waters were treated with carbon nanotubes. The quantities of adsorbed biophenols were studied as a function of the quantities of carbon nanotubes used and the contact time. The experimental conditions for obtaining both the highest possible quantities of biophenol and a purer adsorbate with the highest percentage of biophenols were studied. After the adsorption tests, the vegetation waters were analyzed by UV spectrophotometry to determine, in particular, the variation in the concentration of biophenols. The carbon nanotubes were weighed before and after each adsorption test. In addition, kinetic studies of the adsorption processes were considered. Carbon nanotubes proved their effectiveness in recovering biophenols.

Four different types of multi-walled carbon nanotubes (MWCNTs) were used and compared for the treatment of benzoic acid contaminated water. The types of nanotubes used were: (1) non-purified (CNTs^UP), as made; (2) purified (CNTs^P), not containing the catalyst; (3) oxidized (CNTs^OX), characterized by the presence of groups such as, –COOH; (4) calcined (CNTs⁹⁰⁰), with elimination of interactions between nanotubes. In addition, activated carbon was also used to allow for later comparison. The adsorption tests were conducted on an aqueous solution of benzoic acid at concentration of 20 mg/L, as a model of carboxylated aromatic compounds. After the adsorption tests, the residual benzoic acid concentrations were measured by UV-visible spectrometry, while the carbon nanotubes were characterized by TG and DTA thermal analyses and electron microscopy (SEM). The results show that the type of nanotubes thermally treated at 900 °C has the best performances in terms of adsorption rate and amounts of collected acid, even if compared with the performance of activated carbons.

Artists from the time of Mesopotamia or Egypt and in the Middle Ages astonished us with various coloured Stained-glass windows, prepared with the help of metal nanoparticles. The paper will deal with zeolites, nanoparticles and carbon nanotubes. The latter will be developed more extensively, because we have founded the Nanocyl company, selling carbon nanotubes and it has become the best European company. One carbon nanotube is 100,000 times thinner than a human hair, it is very light – twice as light as aluminium –, its mechanical resistance is much higher than that of steel and it conducts electricity better than metal conductors. The use of carbon nanotubes is very important in nanotechnology. For example, with the help of coiled carbon nanotubes, the weight of a single nanoparticle can be measured, it is equal to one femtogram (10⁻¹⁵ gram). Carbon nanotubes are used in car spray painting to cancel the build-up of static electricity. With the help of carbon nanotubes, it is possible to decrease the velocity of flame propagation, when they are included in composite materials. Carbon nanotubes are also very good as sensors for toxic gases. Their uses will take up the most part of this paper. The future of nanotechnology will be illustrated by nanomachines, by the lift between the Earth and the Moon, and by graphene (one single sheet of graphite). The use of carbon nanotubes will be evoked in waste water cleaning, in the production of drinking water from seawater.