Huanbo Wang

To comparatively study the effects of cold plasma activation and chemical treatment on the adsorption capacities of biomass carbon nanofiber membranes (BCNMs), microcrystalline cellulose (MCC) and chitosan (CS) were used to fabricate porous BCNMs by electrospinning and carbonization. Two modification methods, including oxygen (O₂) plasma activation and chemical treatment using nitric acid (HNO₃), sulfuric acid (H₂SO₄), hydrogen peroxide (H₂O₂), and urea, were further employed to enhance their adsorption performance. Various carbonyl group (C=O), ether bond (C-O), carboxyl group (O-C=O) and pyridinic nitrogen (N), pyrrolic N, and quaternary N functional groups were successfully introduced onto the surface of the BCNMs by the two methods. The BCNM-O₂ showed optimal formaldehyde absorption capacity (120.67 mg g⁻¹), corresponding to its highest contents of N, O-containing functional groups, and intact network structure. However, chemical treatment in strong acid or oxidative solutions destructed the microporous structures and changed the size uniformity of fibers in the BCNMs, resulting in a decline in formaldehyde adsorption capacity. A synergistically physical–chemical adsorption took place during formaldehyde adsorption by the modified biomass nanofiber membranes, due to the coexistence of suitable functional groups and porous structures in the membranes.

The development of biomass-based composites has greatly reduced the daily consumption of plastics. However, these materials are rarely recyclable, thus, posing a severe threat to the environment. Herein, we designed and prepared novel composite materials with ultra-high biomass (i.e., wood flour) filling capacity and good closed-loop recycling properties. The dynamic polyurethane polymer was polymerized in situ on the surface of wood fiber, and then they were hot-pressed into composites. Fourier-transform infrared (FTIR), scanning electron microscopy (SEM), and dynamic thermomechanical analysis (DMA) measurements reveal good compatibility between the polyurethane and wood flour in the composites when the wood flour content is ≤80 wt%. The maximum tensile and bending strength of the composite are 37 and 33 MPa when the wood flour content is 80%. The higher wood flour content results in higher thermal expansion stability and creep resistance in the composites. Moreover, the thermal debonding of dynamic phenol–carbamate bonds facilitates the composites to undergo physical and chemical cycling. The recycled and remolded composites exhibit good mechanical property recovery rates and retain the chemical structures of the original composites.

The removal of rice straw extractives increases the interphase adhesion between rice straw and the high-density polyethylene (HDPE) matrix, while eradicating the inner defects of rice straw/HDPE composites. This study investigated the effect of rice straw extractives removal on the dimensional stability (water uptake and thermal expansion), dynamic mechanical properties, creep, and stress relaxation of rice straw/HDPE composites. Cold water (CW), hot water (HW), and 1% alkaline solution (AL) extraction methods were utilized to remove rice straw extractives. Extracted and unextracted rice straws were mixed with HDPE, maleated polyethylene (MAPE), and Polyethylene wax to prepare composites via extrusion. Removal of rice straw extractives significantly improved the dimensional stability, dynamic mechanical properties, and creep and stress relaxation of rice straw/HDPE composites, with the exception of the thickness swelling of the AL/HDPE and the thermal expansion of the rice straw/HDPE composites. HW/HDPE exhibited the best comprehensive performance.