Youn-Geun Kim

Operando scanning tunneling microscopy first revealed that application of a CO₂-reduction potential to a Cu(pc) electrode in 0.1 M KOH resulted in the reconstruction of the selvedge to an x-layer stack of well-ordered Cu(100) terraces, Cu(pc)-x[Cu(100)]. Subsequent Cu↔Cu₂O oxidation-reduction cycles between −0.90 V and 0.10 V SHE converted the reconstructed region to a stepped Cu(S)-[3(100) × (111)], or Cu(511), surface. Differential electrochemical mass spectrometry showed that reduction of CO produced only CH₃CH₂OH at the lowest overpotential. Later application of STM and surface infrared spectroscopy uncovered a potential, above which no CO adsorption occurs. In this study, electrochemical quartz crystal nanobalance was combined with STM and DEMS as a prelude to the acquisition of CO coverages as continuous functions of concentration and potential; in heterogeneous catalysis, surface coverage are important since the reaction rate are functions of those quantities. Also equally critical is the knowledge of the packing arrangement at the onset of the reaction because, if “CO dimers” were indeed the precursors to C₂₊ products, reduction can only be initiated when the adlayer consists of closely packed CO; otherwise, dimerization will not transpire if the molecules were far apart. The results indicate that the catalysis lags the adsorption, and starts only when CO adsorption is saturated.

Germanene is a single layer allotrope of Ge, with a honeycomb structure similar to graphene. This report concerns the electrochemical formation of germanene in a pH 4.5 solution. The studies were performed using in situ Electrochemical Scanning Tunneling Microscopy (EC-STM), voltammetry, coulometry, surface X-ray diffraction (SXRD) and Raman spectroscopy to study germanene electrodeposition on Au(111) terraces. The deposition of Ge is kinetically slow and stops after 2–3 monolayers. EC-STM revealed a honeycomb (HC) structure with a rhombic unit cell, 0.44 ± 0.02 nm on a side, very close to that predicted for germanene in the literature. Ideally the HC structure is a continuous sheet, with six Ge atoms around each hole. However, only small domains, surrounded by defects, of this structure were observed in this study. The small coherence length and multiple rotations domains made direct observation with surface X-ray diffraction difficult. Raman spectroscopy was used to investigate the multi-layer Ge deposits. A peak near 290 cm⁻¹, predicted to correspond to germanene, was observed on one particular area of the sample, while the rest resembled amorphous germanium. Electrochemical studies of germanene showed limited stability when exposed to oxygen.

Significance: Anthropogenic global warming necessitates the development of renewable carbon-free and carbon-neutral technologies for the future. Electrochemical CO ₂ reduction is one such technology that has the potential to impact climate change by enabling sustainable routes for the production of fuels and chemicals. Whereas the field of CO ₂ reduction has attracted great interest, current state-of-the-art electrocatalysts must be improved in product selectivity and energy efficiency to make this pathway viable for the future. Here, we investigate how controlling the surface structure of copper electrocatalysts can guide CO ₂ reduction activity and selectivity. We show how the coordination environment of Cu surfaces influences oxygenate vs. hydrocarbon formation, providing insights on how to improve selectivity and energy efficiency toward more valuable CO ₂ reduction products.