Tetsuya Yamaki

In this work, we performed transient reflection measurements using the pump–probe protocol to investigate the influence of lattice defects induced by 380 keV argon (Ar) ions on the phonon dynamics of interlayer shearing (E2g1) and in-plane carbon stretching (E2g2) modes in highly oriented pyrolytic graphite (HOPG). The frequency and decay rate of E2g1- and E2g2-mode phonons were changed significantly at the fluence of 1×1014 ions/cm2. This indicated that significant structural changes in HOPG due to 380 keV Ar-ion irradiation were expressed as changes in the frequency and decay rate of phonons. In HOPG irradiated with 380 keV Ar+ at the fluence of 1×1014 ions/cm2, our measurement results indicated that compressive and tensile stresses contributed to in-plane and interlayer graphite structures, respectively.

Emerging immersive high–dynamic range display technologies require not only high peak luminance but also true black levels with hemispherical reflectance below 0.001 (0.1%) to accommodate the wide dynamic range of the human eye (~10 ⁵ ). Such low reflectance materials, denoted here as “supreme black,” must exhibit near-perfect surface antireflection, extremely low in-matrix backscattering, and sufficient optical thickness, which, to date, have only been achieved by fragile sparse materials. We demonstrate a record-low hemispherical reflectance below 0.0002 (absorptance above 0.9998) in a touchproof material by satisfying the three requirements with a superwavelength surface microtexture with nanolevel details, low Mie backscattering composition, and optional additional underlayer. Our supreme black finishes are one to two orders of magnitude blacker than previously developed touchproof super-black materials. Thereby, unprecedented black levels enabling an ambient contrast ratio of ≳10 ⁴ would be provided in display devices, contributing to immersive visual experiences that are critical for seamless remote collaboration and reliable virtual health care.

Glassy carbon substrates were implanted with 100 keV platinum ions. The implanted samples were analyzed using cross-sectional transmission electron microscopy (TEM) and x-ray photoelectron spectroscopy. Ion beam sputtering significantly affected the depth profile during platinum-ion implantation. Cross-sectional TEM revealed that the implanted platinum atoms were in the amorphous state and did not aggregate. Chemical state analysis of the platinum-ion-implanted glassy carbon substrates suggested that lattice defects in the substrates owing to the platinum-ion implantation caused the platinum–carbon interaction with electron transfer from platinum to carbon.

In the global framework of Sustainable Development Goals (SDGs), the Japanese government, like many other goverments of industrialized countries, declared its plan to go carbon neutral in real terms by 2050. This paper describes the application of quantum–beam–based technology to the R&Ds of ion–exchange membranes toward the 2050 carbon neutrality. The gamma–ray or electron–beam induced grafting offers a better way to prepare cation– and anion–exchange membranes (CEMs and AEMs). The approach using ion–track technology results in the preparation of “nano–structure controlled” CEMs and AEMs, which have perfect one–dimensional ion–conductive pathways parallel to their thickness direction. The hierarchical structures of the CEMs and AEMs, ranging from nanometers to micrometers, are revealed by small–angle scattering experiments using a cold or thermal neutron beam. I believe that quantum–beam technology can be developed as a powerful tool in the field of high–efficiency electrochemical energy devices and systems.

The micro/nanocone structures of noble metals play a critical role as heterogeneous electrocatalysts that provide excellent activity. We successfully fabricated platinum cones by electrodeposition using non-penetrated porous membranes as templates. This method involved the preparation of template membranes by the swift-heavy-ion irradiation of commercially available polycarbonate films and subsequent chemical etching in an aqueous NaOH solution. The surface diameter, depth, aspect ratio and cone angle of the resulting conical pores were controlled in the ranges of approximately 70–1500 nm, 0.7–11 μm, 4–12 and 5–13°, respectively, by varying the etching conditions, which finally produced size- and shape-controlled platinum cones with nanotips. In order to demonstrate the electrocatalytic activity, electrochemical measurements were performed for the ethanol oxidation reaction. The oxidation activity was found to be up to 3.2 times higher for the platinum cone arrays than for the platinum plate. Ion-track etching combined with electrodeposition has the potential to be an effective method for the fabrication of micro/nanocones with high electrocatalytic performance.