Alexander V. Egorov

Liquid radioactive waste injected into deep geologic horizons poses a long-term hazard for the environment. Uranium-238, a major component of the nuclear fuel cycle and radioactive waste, has long half-life, high mobility, high toxicity, and complex chemical behavior. Sorption is a crucial process for the radionuclides retention in geosphere and isolation of the waste. In the present work, sorption of U(VI) on the sediments from Severny deep disposal site (Krasnoyarsk, Russia) and reference minerals (quartz and clay) was studied in laboratory-simulated low-level alkaline liquid radioactive waste solutions. U sorption behavior is strongly pH-dependent. It was determined that in the wide pH range U uptake is mostly controlled by quartz in the specific conditions. As uranyl-carbonate complexes play important role in the alkaline medium, carbonate concentration affects the U retention. Contribution of the aquifer constituent minerals was estimated using autoradiography method. Surface complexation reactions for U(VI) sorption on the aquifer sediments were modelled.

KPuO ₂ CO ₃ solid phase precipitation from hexavalent plutonium solution: structure and stability area.

A facile and environmentally benign method for single-phase barium titanate synthesis in a water vapor medium was studied to reveal the mechanism of phase transformation of the initial simple oxide mixture and estimate the capability of the product to be used as a raw material for low-frequency dielectric ceramics. The composition and structure of the reactants’ mixture, treated in vapor at 130–150 °C as well as at 230 °C for various time periods, were investigated by means of XRD, SEM, TEM, EDX, and FTIR methods. The kinetics of the occurring phase transformation can be described using the Johnson–Mehl–Avrami–Erofeev equation. The reaction between the initial oxides was considered as a topochemical process with an apparent activation energy of 75–80 kJ mol⁻¹. A crucial role in this process belonged to the water vapor medium, which facilitated the generation of the reaction zone and the spreading inward of the solid particles. The synthesized tetragonal barium titanate powder (mean particle size of 135 nm) was sintered using a conventional technique at 1250 °C to obtain ceramics with grains of about 2 μm. Capacitance measurements identified a permittivity and dielectric loss factor of the ceramics that reached 3879 and 6.7 × 10⁻³, respectively, at 1 kHz and room temperature.

A facile and environmentally benign method for a single-phase barium titanate synthesis in water vapor medium was studied to reveal the mechanism of phase transformation of the initial simple oxides mixture and estimate the capability of the product to be used as a raw material for low-frequency dielectric ceramics. The composition and structure of the reaction mixture treated in vapor at 130…150 °C as well as 230 °C for various time were investigated by means of XRD, SEM, HRTEM, EDX, and FTIR methods. The kinetics of the occurring phase transformation was described by Johnson-Mehl-Avrami-Erofeev equation. The reaction between the initial oxides was considered as a topochemical process with an apparent activation energy of 74…80 kJ mol^-1. A crucial role in this process belonged to the water vapor medium, which facilitated the generation of the reaction zone and its spreading inward the solid particles. The synthesized tetragonal barium titanate powder (mean particle size of 135 ± 24 nm) was sintered by a conventional technique at 1250 °C to obtain ceramics with grains of about 2 μm. Capacitance measurements performed a dielectric constant and loss tangent of ceramics, which reached 3879 and 6.7 10^-3, respectively, at 1 kHz and room temperature.

This research is focused on the adsorption modification of detonation nanodiamond surfaces with antibiotics for their further use as smart materials for cardiovascular surgery purposes, namely as bioprostheses modifiers. Tritium-labeled amikacin and levofloxacin were used as tracers for the adsorption process control. We found that nanodiamonds form adsorption complexes with levofloxacin via physical adsorption, while in the case of amikacin, electrostatic attraction contributes to the formation of more stable complexes, even in the presence of electrolytes and desorbing agents (models of biological fluids). Antimicrobial characterization of nanodiamond–levofloxacin and nanodiamond–amikacin complexes indicates a reduction in the dose of antibiotics that is used as an antimicrobial agent. Therefore, the use of biomaterial based on DND complexes with antibiotics as the basis of bioprostheses will allow one either to avoid or significantly reduce the duration and intensity of antibiotics use in the postoperative period, which is critically important from the viewpoint of the development of antibiotic resistance in pathogens.

Nanosized bimetallic PtMo, PtFe and trimetallic PtMoSn catalysts deposited on highly dispersed carbon black Vulcan XC-72 were synthesized from the cluster complex compounds PtCl(P(C₆H₅)₃)(C₃H₂N₂(CH₃)₂)Mo(C₅H₄CH₃)(CO)₃, Pt(P(C₆H₅)₃)(C₃N₂H₂(CH₃)₂)Fe(CO)₃(COC₆H₅C₂C₆H₅), and PtCl(P(C₆H₅)₃)(C₃N₂H₂(CH₃)₂)C₅H₄CH₃Mo(CO)₃SnCl₂, respectively. Structural characteristics of these catalysts were studied using X-ray diffraction (XRD), microprobe energy dispersive spectroscopy (EDX), and transmission electron microscopy (TEM). The synthesized catalysts were tested in aqueous 0.5 M H₂SO₄ in a three-electrode electrochemical cells and in single fuel cells. Electrocatalytic activity of PtMo/C and PtFe/C in the oxygen reduction reaction (ORR) and the activity of PtMoSn/C in electrochemical oxidation of ethanol were evaluated. It was shown that specific characteristics of the synthesized catalysts are 1.5–2 times higher than those of a commercial Pt(20%)/C catalyst. The results of experiments indicate that PtFe/C, PtMo/C, and PtMoSn/C catalysts prepared from the corresponding complex precursors can be regarded as promising candidates for application in fuel cells due to their high specific activity.