Ivaylo Hinkov

In this work, we present an efficient and rapid green method for silver nanoparticles synthesis by using extract from Sideritis Scardica and direct sunlight irradiation. The synthesized nanoparticles were characterized by UV-Vis spectroscopy and Transmission Electron Microscopy (TEM). Then, the as obtained silver nanoparticles were mixed with water-based varnish, which is widely used for paperboard packaging in the food industry, pharmaceutical industry and others. Evaluation of the results of a microbiological study showed that water-based varnish with incorporated silver nanoparticles exhibited antibacterial activity against Escherichia coli K12 NBIMCC 407 bacteria and Bacillus subtilis NBIMCC 3562 bacteria. From the results obtained it is clear that these water-based and UV coatings with incorporated silver nanoparticles could find industrial applications in medicine and food industry as packaging with antibacterial properties.

We performed numerical simulations to determine the effect of the most influential operating parameters on the performance of a radio frequency (RF) induction-heating system in which RF magnetic fields inductively heat metal foils to grow graphene. The thermal efficiency of the system depends on the geometry as well as on the materials’ electrical conductivity and skin depth. The process is simulated under specific graphene and two-dimensional (2D) materials growth conditions using finite elements software in order to predict the transient temperature and magnetic field distribution during standard graphene and 2D materials growth conditions. The proposed model considers different coil Helmholtz-like geometries and 11 metal foils, including Ag, Au, Cu, Ni, Co, Pd, Pt, Rh, Ir, Mo, and W. In each case, an optimal window of process variables ensuring a temperature range of 1035 °C–1084 °C or 700 °C–750 °C suitable for graphene and MoS₂ growth, respectively, was found. Temperature gradients calculated from the simulated profiles between the edge and the center of the substrate showed a thermal uniformity of less than ∼2% for coinage metals like Au, Ag, and Cu and up to 7% for Pd. Model validation was performed for graphene growth on copper. Due to its limited heat conductivity, good heating uniformity was obtained. As a consequence, full coverage of monolayer graphene on copper with few defects and a grain domain size of ∼2 µm was obtained. The substrate temperature reached ∼1035 °C from ambient after only ∼90 s, in excellent agreement with model predictions. This allows for improved process efficiency in terms of fast, localized, homogeneous, and precise heating with energy saving. Due to these advantages, inductive heating has great potential for large-scale and rapid manufacturing of graphene and 2D materials.

In this paper, we report on a modified arc process to synthetize graphene, copper and zinc oxide graphene hybrids. The anode was made of pure graphite or graphite mixed with metals or metal oxides. After applying a controlled direct current, plasma is created in the interelectrode region and the anode is consumed by eroding. Continuous and abundant flux of small carbon, zinc or copper species, issued from the anode at a relatively high temperature, flows through the plasma and condenses in the vicinity of a water-cooled cathode leading to few-layered graphene sheets and highly ordered carbon structures. When the graphite rod is filled with copper or zinc oxide nanoparticles, few layers of curved graphene films were anchored with spherical Cu and ZnO nanoparticles leading to a one-step process synthesis of graphene hybrids, which combine the synergetic properties of graphene along with nanostructured metals or semiconducting materials. The as-prepared samples were characterized by Raman spectroscopy, X-ray diffraction (XRD), spatially resolved electron energy loss spectroscopy (EELS), energy filtered elemental mapping and transmission electron microscopy (TEM). In addition to the experimental study, numerical simulations were performed to determine the velocity, temperature and chemical species distributions in the arc plasma under specific graphene synthesis conditions, thereby providing valuable insight into growth mechanisms.

We report on the design of a reactor to grow graphene via inductively heating of copper foils by radio frequency (RF) magnetic fields. A nearly uniform magnetic field induced by Helmholtz-like coils penetrates the copper foil generating eddy currents. While the frequency of the current is being rapidly varied, the substrate temperature increases from room temperature to ~1050 °C in 60 s. This temperature is maintained under Ar/H₂ flow to reduce the copper, and under Ar/H₂/CH₄ to nucleate and grow the graphene over the entire copper foil. After the power cut-off, the temperature decreases rapidly to room temperature, stopping graphene secondary nucleation. Good quality graphene was obtained and transferred onto silicon, and coated with a 300 nm layer of SiO₂ by chemical etching of the copper foil. After synthesis, samples were characterized by Raman spectroscopy. The design of the coils and the total power requirements for the graphene induction heating system were first estimated. Then, the effect of the process parameters on the temperature distribution in the copper foil was performed by solving the transient and steady-state coupled electromagnetic and thermal problem in the 2D domain. The quantitative effects of these process parameters were investigated, and the optimization analysis results are reported providing a root toward a scalable process for large-sized graphene.

In this article, we report on some of the fundamental chemical and physical processes responsible for the deposition of graphene by microwave plasma-enhanced chemical vapor deposition. The graphene is grown by plasma decomposition of a methane and hydrogen mixture (CH ₄ /H ₂ ) at moderate pressures over polycrystalline metal catalysts. Different conditions obtained by varying the plasma power (300–400 W), total pressure (10–25 mbar), substrate temperature (700 °C–1000 °C), methane flow rate (1–10 sccm) and catalyst nature (Co–Cu) were experimentally analyzed using the in situ optical emission spectroscopy technique to assess the species rotational temperature of the plasma and the H-atom relative concentration. Then, two modeling approaches were developed to analyze the plasma environment during graphene growth. As a first approximation, the plasma is described by spatially averaged bulk properties, and the species compositions are determined using kinetic rates in the transient zero-dimensional (0D) configuration. The advantage of this approach lies in its small computational demands, which enable rapid evaluation of the effects of reactor conditions and permit the identification of dominant reactions and key species during graphene growth. This approach is useful for identifying the relevant set of species and reactions to consider in a higher-dimensional model. The reduced chemical scheme was then used within the self-consistent two-dimensional model (2D) to determine auto-coherently the electromagnetic field, gas and electron temperatures, heavy species, and electron and ion density distributions in the reactor. The 0D and 2D models are validated by comparison with experimental data obtained from atomic and molecular emission spectra.

The antimicrobial activity of nanoparticles (NPs) depends of the surface area in contact with microorganisms. The large surface area of the nanoparticles enhances their interaction with the microbes. In this work, a green, simple, rapid, and efficient ultrasound-assisted reduction method for silver nanoparticles (AgNP) synthesis is presented. For the synthesis, an aqueous solution of silver nitrate, ethanol, and ammonia was used. The adopted method can be easily implemented for any kind of scientific or industrial application due to its cost-effective nature. The effect of sonication time on the nanoparticle formation was investigated. Silver nanoparticles were analyzed through transmission electron microscopy and UV-vis spectroscopy. Antimicrobial additives can be incorporated in mass in different matrixes (polymeric or cellulosic), which is a convenient methodology to achieve antimicrobial activity. In this work, silver nanoparticles were incorporated in cellulose using an ultrasonic bath technique. The most important aspect of cellulose containing silver nanoparticles prepared by this method is its high antimicrobial efficiency. The microbiological study was carried out by a standard agar technique. The analysis showed that cellulose with incorporated silver nanoparticles exhibited strong antimicrobial activity against Escherichia coli bacteria. This makes it a promising antibacterial material for food packaging.