Andrea Tummino

The interfacial structure and morphology of films spread from hyperbranched polyethylene imine/sodium dodecyl sulfate (PEI/SDS) aggregates at the air/water interface have been resolved for the first time with respect to polyelectrolyte charged density. A recently developed method to form efficient films from the dissociation of aggregates using a minimal quantity of materials is exploited as a step forward in enhancing understanding of the film properties with a view to their future use in technological applications. Interfacial techniques that resolve different time and length scales, namely, ellipsometry, Brewster angle microscopy, and neutron reflectometry, are used. Extended structures of both components are formed under a monolayer of the surfactant with bound polyelectrolytes upon film compression on subphases adjusted to pH 4 or 10, corresponding to high and low charge density of the polyelectrolyte, respectively. A rigid film is related to compact conformation of the PEI in the interfacial structure at pH 4, while it is observed that aggregates remain embedded in mobile films at pH 10. The ability to compact surfactants in the monolayer to the same extent as its maximum coverage in the absence of polyelectrolyte is distinct from the behavior observed for spread films involving linear polyelectrolytes, and intriguingly evidence points to the formation of extended structures over the full range of surface pressures. We conclude that the molecular architecture and charge density can be important parameters in controlling the structures and properties of spread polyelectrolyte/surfactant films, which holds relevance to a range of applications, such as those where PEI is used, including CO₂ capture, electronic devices, and gene transfection.

Reversible control of the 3D structure of polyelectrolyte/surfactant films at the air/water interface is showcased.

The application of protein deuteration and high flux neutron reflectometry has allowed a comparison of the adsorption properties of lysozyme at the air–water interface from dilute solutions with and without strong denaturants, urea and guanidine hydrochloride (GuHCl). The surface excess and adsorption layer thickness were resolved and complemented by images of the mesoscopic lateral morphology from Brewster angle microscopy. It was revealed that the thickness of the adsorption layer in the absence of added denaturants is less than the short axial length of the lysozyme molecule, which indicates deformation of the globules at the interface. Two-dimensional elongated aggregates in the surface layer merge over time to form an extensive network at the approach to steady state. Addition of denaturants in the bulk results in an acceleration of adsorption and an increase of the adsorption layer thickness. These results are attributed to incomplete collapse of the globules in the bulk as a result of interactions between remote amino acid residues. Both effects may be connected to an increase of the effective total volume of macromolecules due to the changes of their tertiary structure, i.e., the formation of molten globules under the influence of urea and the partial unfolding of globules under the influence of GuHCl. In the former case, the increase of the globule hydrophobicity leads to cooperative aggregation in the surface layer during adsorption. Unlike the case of solutions without denaturants, the surface aggregates are short and wormlike, their size does not change with time, and they do not merge to form an extensive network at the approach to steady state. To the best of our knowledge these are the first observations of cooperative aggregation in lysozyme adsorption layers.

In this work we demonstrate the ability to tune the formation of extended structures in films of poly(sodium styrene sulfonate)/dodecyltrimethylammonium bromide at the air/water interface through control over the charge/structure of aggregates as well as the ionic strength of the subphase. Our methodology to prepare loaded polyelectrolyte/surfactant films from self-assembled liquid crystalline aggregates exploits their fast dissociation and Marangoni spreading of material upon contact with an aqueous subphase. It is proposed as a potential new route to prepare cheap biocompatible films for transfer applications. We show that films spread on water from aggregates of low/negative charge have 1:1 charge binding and can be compressed only to a monolayer, beyond which material is lost to the bulk. For films spread from compact aggregates of positive charge, however, extended structures of the two components are created upon spreading or upon compression of the film beyond a monolayer. The application of ellipsometry, Brewster angle microscopy and neutron reflectometry as well as measurements of surface pressure isotherms allow us to reason that formation of extended structures is activated by aggregates embedded in the film. The situation upon spreading on 0.1 M NaCl is different as there is a high concentration of small ions that stabilize loops of the polyelectrolyte upon film compression, yet extended structures of both components are only transient. Analogy of the controlled formation of extended structures in fluid monolayers is made to reservoir dynamics in lung surfactant. The work opens up the possibility to control such film dynamics in related systems through the rational design of particles in the future.

We describe a new methodology to prepare loaded polyelectrolyte/surfactant films at the air/water interface by exploiting Marangoni spreading resulting from the dynamic dissociation of hydrophobic neutral aggregates dispensed from an aqueous dispersion. The system studied is mixtures of poly(sodium styrene sulfonate) with dodecyl trimethylammonium bromide. Our approach results in the interfacial confinement of more than one third of the macromolecules in the system even though they are not even surface-active without the surfactant. The interfacial stoichiometry of the films was resolved during measurements of surface pressure isotherms in situ for the first time using a new implementation of neutron reflectometry. The interfacial coverage is determined by the minimum surface area reached when the films are compressed beyond a single complete surface layer. The films exhibit linear ripples on a length scale of hundreds of micrometers during the squeezing out of material, after which they behave as perfectly insoluble membranes with consistent stoichiometric charge binding. We discuss our findings in terms of scope for the preparation of loaded membranes for encapsulation applications and in deposition-based technologies.

A novel approach enabling the full control of the 3D nanostructure of polymer thin films is presented. An ordered nanoporous polymer film is obtained using a nanoparticle monolayer as template. The pores are then filled with a second organic component via spin coating which, by modulating the deposition parameters, enables the control of the filling degree with nanometric precision.

It has been known for almost one hundred years that a lower surface tension can be achieved at the air–water interface by spreading protein from a concentrated solution than by adsorption from an equivalent total bulk concentration. Nevertheless, the factors that control this nonequilibrium process have not been fully understood. In the present work, we apply ellipsometry, neutron reflectometry, X-ray reflectometry, and Brewster angle microscopy to elaborate the surface loading of human serum albumin in terms of both the macroscopic film morphology and the spreading dynamics. We show that the dominant contribution to the surface loading mechanism is the Marangoni spreading of protein from the bulk of the droplets rather than the direct transfer of their surface films. The films can be spread on a dilute subphase if the concentration of the spreading solution is sufficient; if not, dissolution of the protein occurs, and only a textured adsorbed layer slowly forms. The morphology of the spread protein films...