The dosimetric characteristics of hydrogel dosimeters based on polyacrylamide (PAC) as a capping agent incorporating silver nitrate as a radiation-sensitive material are investigated using UV-Vis spectrophotometry within the dose range 0–100 Gy. Glycerol was used in the hydrogel matrix to promote the dosimetric response and increase the radiation sensitivity. Upon exposing the PAC hydrogel to γ-ray, it exhibits a Surface Plasmon Resonance (SPR) band at 453 nm, and its intensity increases linearly with absorbed doses up to 100 Gy. The results are compared with the silver nitrate gel dosimeter. Glycerol of 15% in the hydrogel matrix enhances the radiation sensitivity by about 30%. PAC hydrogel dosimeter can be considered a near water equivalent material in the 400 keV–20 MeV photon energy range. At doses less than 15 Gy, the PAC hydrogel dosimeter retains higher radiation sensitivity than the gel dosimeter. The total uncertainty (2σ) of the dose estimated using this hydrogel is about 4%. These results may support the validity of using this hydrogel as a dosimeter to verify radiotherapy techniques and dose monitoring during blood irradiation.

L-Glutamic acid (L-GA) pellets (3.8 mm × 4 mm) and powder dosimeters were studied in the dose range of 0.1–150 kGy using the electron paramagnetic resonance (EPR) technique. The EPR spectra of irradiated L-GA pellets showed an EPR signal with eight lines, and the intensity of the signal increased with an increase of absorbed dose. The results obtained in terms of the energy-absorption coefficients suggest a similar performance of the L-GA pellets as compared to alanine pellets. The value of the temperature coefficient for the L-GA pellets during irradiation was around − 0.08%/°C which is lower than that reported for alanine dosimeter, 0.14%/°C. The influence of humidity on the pellet response was found to be negligible; i.e., the increase in response was only about 2% for a relative humidity of up to 94%. The response of L-GA powder reached stability 4 h after irradiation and continued to be stable until 47 days after irradiation. In contrast, the response of the L-GA pellet dosimeter reached stability 22 h after irradiation and continued to be stable until 8 days after irradiation. For routine applications, the L-GA pellet dosimeter should be analyzed during the stable period after irradiation, to minimize the uncertainties in dose assessment. The overall two-sigma uncertainties in absorbed dose estimation were 5.1% and 3.9% for the dose ranges of 0.1–15 kGy and 15–150 kGy, respectively. It is concluded that L-GA pellets represent a promising dosimeter material for quantification of radiation doses in food irradiation, medical sterilization and polymer modification.