Postconsumer polyolefins (r-POs) are leading plastic waste contributors today. This study reports, for the first time, the compatibilization of r-POs at a 50 kilogram (kg) scale with a styrene block copolymer compatibilizer in the presence of paraffin waxes as rheology modifiers (RMs). The addition of the rheological modifier (RM) and compatibilizer enhances the melt flow indices (MFIs) and mechanical properties, respectively. One aspect of this study is to compare the effectiveness of low-cost paraffin wax to that of specialized and expensive RMs in r-POs. The mechanical and rheological properties such as the melt flow index (MFI) of r-POs were compared in the presence of two types of RMs. Next, the study explores the challenges encountered when scaling the compatibilization of r-POs in the presence of paraffin wax from a 10-g to a 50-kg scale. The mechanical properties were determined and compared for samples at different scales. The study further investigated the effect of the method used for blending paraffin wax with r-PO and its impact on the value of their MFI and mechanical properties. This at-scale validation could pave the way for the commercialization of r-POs.

Hydrophobization of MMT with a reactive ADM₁₈ molecule and its encapsulation into polystyrene latex particles via miniemulsion polymerization.

Poly(ethylene terephthalate) (PET), both bottle grade (PET‐B) and thermoform grade (PET‐T), are widely used in the packaging sector. However, only PET‐B is recycled and reused, while PET‐T needs to be separated from recycled PET bales. This study aims to assess the impact of solid‐state polymerization (SSP), chain extension and the combination of chain extension–SSP to transform PET‐B and PET‐T blends into PET‐T‐like material. The intrinsic viscosity (IV) values for PET‐B blends with 10–20 wt% of PET‐T are measured for the samples obtained in this study. The mechanical properties, such as tensile strength, modulus, elongation and impact strength, were also determined. The glass transition temperature, melting temperature, crystallinity and thermal degradation were also investigated. The findings suggest that the combination of SSP and chain extension leads to a significant improvement in IV and tensile strength, while SSP alone is less suitable to offer the desired IV values. © 2024 The Authors. Polymer International published by John Wiley & Sons Ltd on behalf of Society of Industrial Chemistry.

Glycidyl-based chain extenders are broadly used as processing aids to enhance the physical properties of polyesters, but glycidyl-containing compounds have severe toxicity concerns.