Theodoros Tsoufis

This work elucidates the influence of graphene (G) and graphene oxide (GO) content on the desalination performance and scaling characteristics of G/polyvinylidene fluoride (G/PVDF) mixed matrix and GO/PVDF composite‐skin membranes, applied in a direct contact membrane distillation process (DCMD). Inclusion of high quality, nonoxidized, monolayered graphene sheets as polymer membrane filler, and application of a novel GO/water‐bath coagulation method for the preparation of the GO/PVDF composite films, took place. Water permeability and desalination tests via DCMD, revealed that the optimal G content was 0.87 wt%. At such concentration the water vapor flux of the G/PVDF membrane was 1.7 times that of the nonmodified reference, while the salt rejection efficiency was significantly improved (99.8%) as compared to the neat PVDF. Similarly the GO/PVDF surface‐modified membrane, prepared using a GO dispersion with low concentration (0.5 g/L), exhibited twofold higher water vapor permeate flux as compared to the neat PVDF, but however, its salt rejection efficiency was moderate (80%), probably due to pore wetting during DCMD. The relatively low scaling tendency observed for both G and GO modified membranes is primarily attributed to their smoother surface texture as compared to neat PVDF, while scaling is caused by the deposition of calcite crystals, identified by XRPD analysis. POLYM. ENG. SCI., 59:E262–E278, 2019. © 2018 Society of Plastics Engineers

The presentation will focus on CO₂ adsorption by metal organic frameworks (MOFs), graphene oxide (GO), MOF/GO composites, as well as their amine-functionalized analogues.

Hydrophilic oxidized carbon nanodiscs able to be used as drug delivery system and as support in nanobiocatalytic applications.

We report a facile approach for the in situ synthesis of very small iron oxide nanoparticles on the surface of high-quality graphene sheets. Our synthetic strategy involved the direct, liquid-phase exfoliation of highly crystalline graphite (avoiding any oxidation treatment) and the subsequent chemical functionalization of the graphene sheets via the well-established 1,3-dipolar cycloaddition reaction. The resulting graphene derivatives were employed for the immobilization of the nanoparticle precursor (Fe cations) at the introduced organic groups by a modified wet-impregnation method, followed by interaction with acetic acid vapours. The final graphene-iron oxide hybrid material was achieved by heating (calcination) in an inert atmosphere. Characterization by X-ray diffraction, transmission electron and atomic force microscopy, Raman and X-ray photoelectron spectroscopy gave evidence for the formation of rather small (<12 nm), spherical, magnetite-rich nanoparticles which were evenly distributed on the surface of few-layer (<1.2 nm thick) graphene. Due to the presence of the iron oxide nanoparticles, the hybrid material showed a superparamagnetic behaviour at room temperature.

Experimental and theoretical studies are performed in order to illuminate, for first time, the intercalation mechanism of polycyclic aromatic molecules into graphite oxide. Two representative molecules of this family, aniline and naphthalene amine are investigated. After intercalation, aniline molecules prefer to covalently connect to the graphene oxide matrix via chemical grafting, while napthalene amine molecules bind with the graphene oxide surface through π–π interactions. The presence of intercalated aromatic molecules between the graphene oxide layers is demonstrated by X‐ray diffraction, while the type of interaction between graphene oxide and polycyclic organic molecules is elucidated by X‐ray photoelectron spectroscopy. Combined quantum mechanical and molecular mechanical calculations describe the intercalation mechanism and the aniline grafting, rationalizing the experimental data. The present work opens new perspectives for the interaction of various aromatic molecules with graphite oxide and the so‐called “intercalation chemistry”.