Donovan N. Leonard

The U.S. Department of Energy's Office of Scientific and Technical Information

The U.S. Department of Energy's Office of Scientific and Technical Information

The U.S. Department of Energy's Office of Scientific and Technical Information

This report investigates a laser-interference surface treatment as a non-contact, i.e., without major solid/liquid medium application or abrasion, and non-chemical surface preparation method for aerospace coating systems. It was proposed to use the laser-interference technique to structure surfaces of Al and/or Ti, creating "rough" surfaces with pre-engineered series of ridges and valleys at submicron scale. The science goal of this study was to develop an understanding of the surface microstructure, topology, and physical mechanisms that would improve adhesion and corrosion protection of Al2024-T3. Microstructure analysis indicates that the laser-interference structuring (LIS) was found to reduce the formation of CuMn-rich precipitates in Al 2024-T3 over a 500-800 nm depth from top surface. The X-cut and cross-hatch coating adhesion ratings indicate that the LIS specimens meet the performance requirements in the coating adhesion specifications by having a higher or identical ranking to those specimens prepared with current state-of-the-art chemical conversion or sulfuric acid anodizing. After the ASTM B117 corrosion exposure, it was found that the laser processed specimens exhibited only few blisters. It was found that the corrosion damage was minimized at a laser rastering speed of 4 mm/s, for which only 33% of specimens developed very minor corrosion damage. The ASTMmore » D1654 creepage ratings, used to evaluate corrosion damage along the scribe lines, were found to be at least nine for all coated panels. These results indicate that the laser-interference technique with the additional acetone wiping has the potential to be further developed as a minor chemical surface preparation technique for chromate-containing epoxy primers coatings.« less

Atomic-resolution scanning transmission electron microscopy reveals the initiation and progression mechanism of microcracks and voids in LiNi_0.8Co_0.15Al_0.05O₂ (NCA) cathodes upon extended charge/discharge cycles.

This joint project among ORNL, GM, and DRO successfully developed ionic liquid-additized low viscosity lubricants, SAE 0W-12 and 70W-80, for both IC engine and rear axle lubrication, respectively, and demonstrated combined vehicle fuel economy improvement (FEI). Phosphonium-alkylphosphate ILs have been found to be the most effective among the candidates in protecting surface damage from both sliding wear and rolling contact fatigue, and optimal IL concentrations have been determined. The IL’s impact on three-way catalyst seems to be significantly less adverse than the conventional ZDDP. Oil formulations were optimized for both energy efficiency and wear protection. Tribological bench testing of the IL-additized low-viscosity oils showed at least 40% lower boundary friction, more than 60% lower elastohydrodynamic friction, and greater than 50% less wear compared with commercial baselines. IL-additized lubricants have demonstrated FEI by 9.9% in engine dynamometer tests under extreme conditions and 6.9% increased power output in gear rig tests. Prototype IL-additized engine oil and rear axle fluid exhibited combined FEI of 1.39% and 3.24% benchmarked against the state-of-the-art baselines in vehicle testing of fresh oils under the Federal Test Procedure (FTP) city cycle and Highway Fuel Economy Driving Schedule (HWFET), respectively. Used oil analysis suggested that the IL-additized low-viscosity oilsmore » produced less wear than the commercial baselines. The gained fundamental understanding and demonstrated FEI in this work pave the way for future development and implementation of the ionic liquid technology.« less

The U.S. Department of Energy's Office of Scientific and Technical Information

The U.S. Department of Energy's Office of Scientific and Technical Information