Fei Li

Here we report a comparative study on the bottom-up synthesis of multi-element hydroxides composed of Mg, Al, Fe and Zn cations to understand the role of solvents. Two common solvents, water and ethylene glycol, a typical polyol, are used. The polyol-derived MgAlFeZn–OH are nanosheets with homogeneous elemental distribution, while the hydrothermal-derived MgAlFeZn–OH are mixtures of plate-like hydroxide layers and rod-like spinel oxides. The coordinating properties and the high viscosity of the ethylene glycol provide the possibility to mediate the hydrolysis rates and to control the particle growth. The high specific surface area of the polyol-derived multi-element hydroxide nanosheets (352.4 m² g⁻¹) guarantees them as excellent adsorbents for adsorbing anionic dyes in aqueous solution.

Hierarchical porous silicon carbide (SiC) attracts great attention due to its superior chemical resistance, high thermal shock resistance, and excellent thermal stability. The preparation of a porous SiC monolith via a simple sol–gel method is limited by either the high cost of the raw materials or the special time-consuming drying process. Herein, we report an ambient drying sol–gel approach for the synthesis of organic–inorganic hybrid monolithic gels which can be converted into hierarchical porous SiC monoliths upon pyrolysis at 1400 °C. The as-synthesized SiC monoliths possess hierarchical pores with macropores of 4.5 µm and mesopores of 2.0 nm. The porosities, specific surface areas and compressive strengths of the hierarchical porous SiC monoliths are 71.3%, 171.5 m²/g and 7.0 ± 0.8 MPa, respectively.

This study aimed to identify a useful high-entropy source for gas detection by spinel oxides that are composed of five cations in nearly equal molar amounts and free of impurities. The sensor responses of the spinel oxides [1# (CoCrFeMnNi)₃O₄, 2# (CoCrFeMnZn)₃O₄, 3# (CoCrFeNiZn)₃O₄, 4# (CoCrMnNiZn)₃O₄, 5# (CoFeMnNiZn)₃O₄, and 6# (CrFeMnNiZn)₃O₄] were evaluated for the test gases (7 ppm NO₂, 5000 ppm H₂, 3 ppm NH₃, and 3 ppm H₂S). In response to NO₂, 1# and 2# showed p-type behavior while 3–6# showed n-type semiconductor behavior. There are three p-type and one n-type AO structural compositions in AB₂O₄[AO·B₂O₃] type spinel, and 1# showed a stable AO composition because cation migration from site B to site A is unlikely. Therefore, it was assumed that 1# exhibited p-type behavior. The p-type behavior of 2# was influenced by Cr oxide ions that were present at the B site and the stable p-type behavior of zinc oxide at the A site. The spinel oxides 3# to 6# exhibited n-type behavior with the other cationic oxides rather than the dominant p-type behavior exhibited by the Zn oxide ions that are stable at the A site. In contrast, the sensor response to the reducing gases H₂, NH₃, and H₂S showed p-type semiconductor behavior, with a particularly selective response to H₂S. The sensor responses of the five-element spinel oxides in this study tended to be higher than that of the two-element Ni ferrites and three-element Ni-Zn ferrites reported previously. Additionally, the susceptibility to sulfurization was evaluated using the thermodynamic equilibrium theory for the AO and B₂O₃ compositions. The oxides of Cr, Fe, and Mn ions in the B₂O₃ composition did not respond to H₂S because they were not sulfurized. The increase in the sensor response due to sulfurization was attributed to the decrease in the depletion layer owing to electron sensitization, as the top surface of the p-type semiconductors, ZnO and NiO, transformed to n-type semiconductors, ZnS and NiS, respectively. High-entropy oxides prepared using the hydrothermal method with an equimolar combination of five cations from six elements (Cr, Mn, Fe, Co, Ni, and Zn) can be used as a guideline for the design of high-sensitivity spinel-type composite oxide gas sensors.

Low-dimensional high-entropy materials, such as nanoparticles and two-dimensional (2D) layers, have great potential for catalysis and energy applications. However, it is still challenging to synthesize 2D layered high-entropy materials through a bottom-up soft chemistry method, due to the difficulty of mixing and assembling multiple elements in 2D layers. Here, we report a simple polyol process for the synthesis of a series of 2D layered high-entropy transition metal (Co, Cr, Fe, Mn, Ni, and Zn) hydroxides (HEHs), involving the hydrolysis and inorganic polymerization of metal-containing species in ethylene glycol media. The as-synthesized HEHs demonstrate 2D layered structures with interlayer distances ranging from 0.860 to 0.987 nm and homogeneous elemental distribution of designed equimolar stoichiometry in the layers. These 2D HEHs exhibit a low overpotential of 275 mV at 10 mA cm⁻² in a 0.1 M KOH electrolyte for the oxygen evolution reaction. Superparamagnetic spinel-type high-entropy nanoparticles can also be obtained by annealing these HEHs. Our polyol approach creates opportunities for synthesizing low-dimensional high-entropy materials with promising properties and applications.