Chandra A. Macauley

Atom probe tomography (APT) is a powerful technique to obtain 3D chemical and structural information, however the ‘standard’ atom probe experimental workflow involves transfer of specimens at ambient conditions. The ability to transfer air- or thermally-sensitive samples between instruments while maintaining environmental control is critical to prevent chemical or morphological changes prior to analysis for a variety of interesting sample materials. In this article, we describe a versatile transfer system that enables cryogenic- or room-temperature transfer of specimens in vacuum or atmospheric conditions between sample preparation stations, a focused ion beam system (Zeiss Crossbeam 540) and a widely used commercial atom probe system (CAMECA LEAP 4000X HR). As an example for the use of this transfer system, we present atom probe data of gallium- (Ga)-free grain boundaries in an aluminum (Al) alloy specimen prepared with a Ga-based FIB.

The sphalerite from the Burgstaetter Gangzug, a vein system of the Upper Harz Mountain nearby the town of Clausthal-Zellerfeld, exhibits a very interesting and partly complementary incorporation pattern of Cu, In and Sb, which has not yet been reported for natural sphalerite. A sphalerite specimen was characterized with electron probe micro-analysis (EPMA) and atom probe tomography (APT). Based on the EPMA results and a multilinear regression, a relation expressed as Cu = 0.98In + 1.81Sb + 0.03 can be calculated to describe the correlation between the elements. This indicates, that the incorporation mechanisms of In and Sb in the structure differ substantially. Indium is incorporated with the ratio Cu:In = 1:1 like in roquesite (CuInS₂), supporting the coupled substitution mechanism 2Zn²⁺ → Cu⁺ + In³⁺. In contrast, Sb is incorporated with a ratio of Cu:Sb = 1.81:1. APT, which has a much higher spatial resolution indicates a ratio of Cu: Sb = 2.28: 1 in the entire captured volume, which is similar to the ratio calculated by EPMA, yet with inhomogeneities at the nanometer-scale. Analysis of the solute distribution shows two distinct sizes of clusters that are rich in Cu, Sb and Ag.

Employing Ag₂Cu₂O₃, a mixed metal oxide, as a template catalyst material for electrochemical reduction of CO enables generation of multi-carbon products with a faradaic efficiency of close to 92%, at a current density of 600 mA cm⁻².

A copper‐oxide‐based catalyst enriched with paramelaconite (Cu₄O₃) is presented and investigated as an electrocatalyst for facilitating electroreduction of CO₂ to ethylene and other hydrocarbons. Cu₄O₃ is a member of the copper‐oxide family and possesses an intriguing mixed‐valance nature, incorporating an equal number of Cu⁺ and Cu²⁺ ions in its crystal structure. The material is synthesized using a solvothermal synthesis route and its structure is confirmed via powder X‐ray diffraction, transmission electron microscope based selected area electron diffraction, and X‐ray photoelectron spectroscopy. A flow reactor equipped with a gas diffusion electrode is utilized to test a copper‐based catalyst enriched with the Cu₄O₃ phase under CO₂ reduction conditions. The Cu₄O₃‐rich catalyst (PrC) shows a Faradaic efficiency for ethylene over 40% at 400 mA cm⁻². At −0.64 versus reversible hydrogen electrode, the highest C₂₊/C₁ product ratio of 4.8 is achieved, with C₂₊ Faradaic efficiency over 61%. Additionally, the catalyst exhibits a stable performance for 24 h at a constant current density of 200 mA cm⁻².