Livia Tosi Trevelin

This study investigated the effect of irradiation with an erbium‐doped yttrium aluminium garnet (Er:YAG) laser and coating with silica on the surface characteristics, bond strength, and flexural strength of dental zirconia. Three hundred and forty‐three standard zirconia specimens were created, and 49 were assigned to each of seven surface treatment groups: (i) no treatment; Er:YAG laser (80 mJ/2 Hz) with pulse widths of 50 μs (ii), 100 μs (iii), 300 μs (iv), or 600 μs (v); or tribochemical silica coating at the partially sintered stage (vi) or after sintering was complete (vii). All specimens were sintered after the surface treatments, except for the group in which specimens were sintered before treatment. The study outcomes were roughness, surface loss, microshear bond strength (μSBS), and biaxial flexural strength (BFS). Mean roughness and surface loss values were significantly higher in specimens from irradiated groups than in those from silica‐coated groups. Regarding μSBS, after aging, specimens from all experimental groups presented very low and similar μSBS values, irrespective of the surface treatment. Silica coating after sintering yielded the highest BFS (1149.5 ± 167.6 MPa), while coating partially sintered specimens with silica resulted a BFS (826.9 ± 60.9 MPa) similar to that of the untreated control group (794.9 ± 101.7 MPa). Laser treatments, irrespective of pulse width used, significantly decreased the BFS. In the group treated with laser at 300 μs pulse width, specimens exhibited the lowest BFS value (514.1 ± 71.5 MPa). Adhesion to zirconia was not stable after aging, regardless of the surface treatment implemented.

The purpose of this study was to explore the influence of Er:YAG laser irradiation with different pulse durations on the organic matrix, micromorphology of the hybrid layer (HL), and bond strength over time. Sixty caries-free human molars were cut to obtain flat dentin surfaces which were randomly divided into 4 groups: control (not irradiated–G1) and laser groups (80 mJ/2 Hz) with pulse duration ranging between 50 (G2), 300 (G3), and 600 μs (G4). A self-etch adhesive system (Universal 3M ESPE) was applied on pre-treated dentin surfaces and cylinders of resin composite were built up and stressed in a universal testing machine (μSBS) at 24 h and after12 months (n = 12). In addition, 3 other dentin-bonded specimens were prepared as previously described for each group with the adhesive doped with 0.1 wt% Rhodamine B to analyze hybrid layer morphology under Confocal Laser Microscope Scanning (CLMS). Organic matrix and collagen fibrils were analyzed by second harmonic generation (SGH). Two-way ANOVA and Tukey’s test detected significantly higher μSBS values for the control group, whereas the lower values were observed in all laser groups at 24 h (p < 0.05). Storage in artificial saliva did not reduce μSBS in all groups. The low signal emitted by SHG images below the irradiated area demonstrated thermal damage of the collagen matrix. CLMS images of laser groups exhibited thicker and irregular resin-dentin interfaces than the control group. Regardless of the pulse duration, Er:YAG laser pre-treatment altered the organic matrix and HL formation which resulted in low μSBS values at 24 h. The alterations on dentin’s organic structure did not jeopardize the μSBS after 1 year of saliva storage.