Esperanza Menéndez

Ternary blended cements, made with silica fume and limestone, provide significant benefits such as improved compressive strength, chloride penetration resistance, sulfates attack, etc. Furthermore, they could be considered low-carbon cements, and they contribute to reducing the depletion of natural resources in reference to water usage, fossil fuel consumption, and mining. Limestone (10%, 15%, and 20%) with different fineness and coarse silica fume (3%, 5%, and 7%) was used to produce ternary cements. The average size of coarse silica fume used was 238 μm. For the first time, the carbonation resistance of ternary Portland cements made with silica fume and limestone has been assessed. The carbonation resistance was assessed by natural carbonation testing. The presence of coarse silica fume and limestone in the blended cement led to pore refinement of the cement-based materials by the filling effect and the C-S-H gel formation. Accordingly, the carbonation resistance of these new ternary cements was less poor than expected for blended cements.

The use of silica fume as a partial replacement for Ordinary Portland Cement provides a wide variety of benefits, such as reduced pressure on natural resources, reduced CO₂ footprint, and improved mechanical and durability properties. The formation of more stable crystallographic phases in the hardened cement paste can promote resistance to concrete attacks. However, using coarse silica fume may result in lower expenses and shorter workdays. In this work, coarse silica fume was used as a partial replacement of cement, by weight, at 3%, 5%, and 7%, and it was used as limestone filler at different particle sizes. The size of coarse silica fume used was 238 μm. The microstructural, compositional analysis, and crystalline phase content of mixed cements at different ages were evaluated. The addition of coarse silica fume and limestone promoted pore refinement of the composites and increased the calcium and silica content. The filling effect of fine limestone and coarse silica fume particles, as well as the formation of CSH gel, was found to be the main reason for the densified microstructure. The contributions of combined coarse silica fume and limestone improve the stability of CSH gels and pozzolanic reaction.

The influence of the effects of the degradation of materials on the seismic fragility of Cultural Heritage buildings in Granada (Spain) is investigated. The degradation of the material, which mainly happens at the lower levels of the façades, is obtained by using 3D photogrammetry data. Fragility curves for three cultural heritage constructions in Granada are calculated by using FE nonlinear dynamic analyses for both non-deteriorated and deteriorated geometries. The Finite Elements (FE) models, based on the macro-modelling technique, are subjected to ground motions for the city of Granada, which were selected by considering Probabilistic Seismic Hazard Analysis (PSHA) methodology with their probability of occurrence. The response of each model is analyzed for different seismic Intensity Measure (IM) levels, which, in this study, correspond to average pseudo-acceleration. The procedure is applied to three monuments in Granada that were built with two different constructions materials: calcarenite and rammed earth. The damage mechanisms considered are roof displacement or maximum compressive principal stress, depending on each case. The results show that the restoration works that have been carried out has prevented structural failures in the rammed earth construction studied, and that, during future seismic events, special attention must be paid to the level of compressive strengh reached in the Santa Pudia calcarenite used at the San Jerónimo monastery.

To create an international recommendation concerning the release of alkalis, test method AAR-8 was developed within the scope of RILEM TC 258-AAA activities. The first round robin test was performed using five aggregate types, and further investigation was conducted as RRT2, leading to the final version of the AAR-8 recommendation. Five aggregates with different mineralogies and origins were immersed in specific volumes of NaOH or KOH solutions with excess calcium hydroxide maintained 38 °C and 60 °C respectively. Samples of the immersion test solution were removed at intervals of 2, 6, 13, 26, and 52 weeks by pipetting and chemically analyzed for NaOH or KOH test solutions. The amount of alkali released was expressed in grams of Na2O, K2O, and Na2Oe per kilogram of the respective aggregate. The results obtained are presented. Based on the data, several changes to the original version of the test method are proposed.

Ternary Portland cements composed of coarse silica fume (SF), limestone (LS), and Portland cement (PC) can afford some environmental advantages by reducing the clinker content in Portland cements. These cements will help to reduce the clinker factor target from 0.78 to 0.60 by 2050 with the aim to be climate neutral. Silica fume (SF) possesses pozzolanic properties that enhance mechanical strength and durability. By contrast, limestone powder has three main outcomes, i.e., filler, dilution, and chemical effects. The first reduces porosity and refines the microstructure of mortars and concretes. The second decreases the amount of hydration products and increases the porosity; the third one promotes the appearance of carboaluminates and reduces porosity. This paper covers the mechanical properties of Portland cement-limestone-coarse silica fume ternary cements, and its synergetic mechanism. Compressive and flexural strength of mortar at 2, 7, 14 and 28 days was performed. Coarse silica fume has a minor contribution on the nucleation effect compared to ground limestone at early ages. The nucleation and filler effects, at early ages, are less pronounced in coarse and very fine limestone powder. The highest compressive strength at 28 days is reached with the lowest content of coarse silica fume (3%). Mortar mixes made with a high level of limestone presented a delay in the compressive strength development.