Helmut Keul

Soft polymer nanocapsules and microgels, which can adapt their shape and, at the same time, sequester and release molecular payloads in response to an external trigger, are a challenging complement to vesicular structures like polymersomes. In this work, we report the synthesis of such capsules by photo-cross-linking of coumarin-substituted polyglycidyl ethers, which we prepared by Williamson etherification of epichlorohydrin (ECH) repeating units with 7-hydroxycoumarin in copolymers with tert-butyl glycidyl ether (tBGE). To control capsule size, we employed the prepolymers in an o/w miniemulsion, where they formed a gel layer at the interface upon irradiation at 365 nm by [2 pi + 2 pi] photodimerization of the coumarin groups. Upon irradiation at 254 nm, the reaction could be reversed and the gel wall could be repeatedly disintegrated and rebuilt. We further demonstrated (i) reversible hydrophilization of the gels by hydrolysis of the lactone rings in coumarin dimers as a mechanism to manipulate the permeability of the capsules and (ii) binding functional molecules as amides. Thus, the presented nanogels are remarkably versatile and can be further used as a carrier system.

Soft polymer nanocapsules and microgels, which can adapt their shape and at the same time sequester and release molecular payloads in response to an external trigger, are a challenging complement to vesicular structures like polymersomes. In this work we report the synthesis of such capsules by photocrosslinking of coumarin-substituted polyglycidyl ethers, which we prepared by Williamson etherification of epichlorohydrin (ECH) repeating units with 7-hydroxycoumarin in copolymers with tert-butyl glycidyl ether (tBGE). To control capsule size, we employed the prepolymers in an o/w miniemulsion, where they formed a gel layer at the interface upon irradiation at 365 nm by [2π+2π] photodimerization of the coumarin groups. Upon irradiation at 245 nm, the reaction could be reversed and the gel wall could be repeatedly disintegrated and rebuilt. We further demonstrated (i) reversible hydrophilization of the gels by hydrolysis of the lactone rings in coumarin dimers as a mechanism to manipulate the permeability of the capsules, and (ii) binding functional molecules as amides. Together with the possibility to hydrolyze the tert-butyl ether group we demonstrate a remarkable versatility of such nanogels for their use as a carrier system.

Gelation in the presence of cells with minimum cytotoxicity is highly desirable for materials with applications in tissue engineering. Herein, the naturally occurring polysaccharide pullulan is functionalized with thiolactones that undergo ring-opening addition of amines. As a result, the modified pullulan can be cross-linked with diamines and/or amine-containing biological substrates enhancing the system's versatility (e.g., gelatin and cell-binding ligands GHK/GRGDS). Thiolactone degrees of substitution of 2.5 or 5.0 mol % are achieved, and respective hydrogels exhibit mesh sizes of 27.8 to 49.1 nm. Cell proliferation studies on chosen gels (G′ ≅ 500 Pa, over 14 days) demonstrate that for normal human dermal fibroblasts (NHDFs), both gelatin and GRGDS equally support cell proliferation, while in the case of hepatocytes (HepG2), the presence of GRGDS and GHK improve cell proliferation 10-fold compared to gelatin. Cells remain viable and in one instance were successfully encapsulated by in situ gelation, altogether confirming the mild and biocompatible nature of this strategy to produce biogels using biologically active substrates as cross-linkers.

Synthetic amphiphilic copolymers with strong antimicrobial properties mimicking natural antimicrobial peptides were obtained via synthesis of an alternating copolymer of maleic anhydride and 4-methyl-1-pentene. The obtained copolymer was modified by grafting with 3-(dimethylamino)-1-propylamine (DMAPA) and imidized in a one-pot synthesis. The obtained copolymer was modified further to yield polycationic copolymers by means of quaternization with methyl iodide and dodecyl iodide, as well as by being sequentially quaternized with both of them. The antimicrobial properties of obtained copolymers were tested against Escherichia coli, Pseudomonas aeruginosa, Staphylococcus epidermidis, and Staphylococcus aureus. Both tested quaternized copolymers were more active against the Gram-negative E. coli than against the Gram-positive S. aureus. The copolymer modified with both iodides was best when tested against E. coli and, comparing all three copolymers, also exhibited the best effect against S. aureus. Moreover, it shows (limited) selectivity to differentiate between mammalian cells and bacterial cell walls. Comparing the minimum inhibitory concentration (MIC) of Nisin against the Gram-positive bacteria on the molar basis instead on the weight basis, the difference between the effect of Nisin and the copolymer is significantly lower.

Enzyme-catalyzed ring-opening polymerization of lactones is a method of increasing interest for the synthesis of polyesters. In the present work, we investigated which changes in the structure of Candida antarctica lipase B (CaLB) shift the catalytic equilibrium between esterification and hydrolysis towards polymerization. Therefore, we present two concepts: (i) removing the glycosylation of CaLB to increase the surface hydrophobicity; and (ii) introducing a hydrophobic lid adapted from Pseudomonas cepacia lipase (PsCL) to enhance the interaction of a growing polymer chain to the elongated lid helix. The deglycosylated CaLB (CaLB-degl) was successfully generated by site-saturation mutagenesis of asparagine 74. Furthermore, computational modeling showed that the introduction of a lid helix at position Ala148 was structurally feasible and the geometry of the active site remained intact. Via overlap extension PCR the lid was successfully inserted, and the variant was produced in large scale in Pichia pastoris with glycosylation (CaLB-lid) and without (CaLB-degl-lid). While the lid variants show a minor positive effect on the polymerization activity, CaLB-degl showed a clearly reduced hydrolytic and enhanced polymerization activity. Immobilization in a hydrophobic polyglycidol-based microgel intensified this effect such that a higher polymerization activity was achieved, compared to the “gold standard” Novozym^® 435.

A synthetic strategy for the light-induced cross-linking and post-cross-linking modification of polyglycidol towards amphiphilic polyethers.

Antimicrobial polymers are an attractive alternative to low molecular weight biocides, because they are non-volatile, chemically stable, and can be used as non-releasing additives. Polymers with pendant quaternary ammonium groups and hydrophobic chains exhibit antimicrobial properties due to the electrostatic interaction between polymer and cell wall, and the membrane disruptive capabilities of the hydrophobic moiety. Herein, the synthesis of cationic–hydrophobic polyglycidols with varying structures by post-polymerization modification is presented. The antimicrobial properties of the prepared polyglycidols against E. coli and S. aureus are examined. Polyglycidol with statistically distributed cationic and hydrophobic groups (cationic–hydrophobic balance of 1:1) is compared to (i) polyglycidol with a hydrophilic modification at the cationic functionality; (ii) polyglycidol with both—cationic and hydrophobic groups—at every repeating unit; and (iii) polyglycidol with a cationic–hydrophobic balance of 1:2. A relationship between structure and properties is presented.

The solubility of terpolymers containing alkyl, and perfluoroalkyl side chains as well as succinic acid moieties in the main chain, P[R_FMA_0.2-co-R_HMA_0.65-co-MAH_0.15] (R_H = C₄H₉- or C₁₂H₂₅-, R_F- = C₁₀H₄F₁₉-) with ca. 20 mol % fluorinated side chains and 10–22 mol % of succinic anhydride rings was tested in a number of solvents varying from water to non polar mineral oils. The polymers are well soluble in fluorinated solvents like Freon-113^® and 1,3-bis(trifluoromethyl) benzene, in semi-polar solvents like chloroform, THF or lower esters and also in hydrocarbons with polymers containing dodecyl methacrylate. In self-emulsification experiments, a stable water emulsion of P[F8H2MA_0.2-co-BMA_0.65-co-MAH_0.15] was obtained. The dispersability and emulsification of these polymers in mixtures of organic solvents and water yielded stable emulsions in the presence of additional surfactant. Thin films coated from organic solutions as well as from emulsions on glass resulted in water and oil-repelling surfaces with contact angles up to 140° against water and 71° against hexadecane. An enhancing effect of annealing was not observed.

Terpolymers of homogeneous composition were prepared by free radical copolymerization of butyl or dodecyl methacrylate, 1H,1H,2H,2H-perfluorodecyl methacrylate and maleic anhydride using the continuous monomer addition technique. The copolymerization reactions were performed at 65 °C in the presence of azobisisobutyronitrile as an initiator in a mixture of methyl ethyl ketone and 1,3-bis (trifluoromethyl)benzene. The monomers and initiator are added to the reaction mixture with the same rate they are consumed in 5- and 10-fold excess compared to the initial monomer stock. The obtained terpolymers with molecular weights M_n = 50,000–70,000 are of uniform composition, close to the composition determined in low conversion experiments, proving the principle of the chosen concept. The kinetic data necessary for the design of the continuous addition experiment were obtained from binary copolymerization experiments at low monomer conversion (to avoid compositional drift). In addition, the so-called terpolymerization parameter was determined from ternary copolymerization experiments.