The goal of this research was to obtain high-density single-walled carbon nanotube forests (SWNTs) on conductive substrates for different applications, including field emission. For this, dip-coating was chosen as the catalyst deposition method, to subsequently grow SWNTs by Alcohol Catalytic Chemical Vapor Deposition (AC-CVD). Si (100) was chosen as the substrate, which was then coated with a TiN thin film. By sputtering with Ar, it was possible to generate alternating TiN and Si lanes, with a different wettability and, therefore, a different affinity for the catalysts. As a result, the Mo-Co catalyst was mainly deposited on TiN and not on sputtered-Si, which allowed the selective growth of SWNT forests on the TiN conductive surfaces. These as-synthesized SWNTs were used for field emission measurements in a high vacuum chamber.

Hollow magnetite microspheres have been synthesized by a simple process through a template-free hydrothermal approach. Hollow microspheres were surface modified by coating with a silica nanolayer. Pristine and modified hollow microparticles were characterized by field-emission electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, FT-IR and Raman spectroscopy, and VSM magnetometry. The potential application of the modified hollow magnetite microspheres as a drug carrier was evaluated by using Rhodamine B and methotrexate as model drugs. The loading and release kinetics of both molecules showed a clear pH and temperature dependent profile.