Heonjoo Ha

This study explores the molecularly templated reaction of pyrene‐terminated telechelic poly(dimethyl siloxane) (PDMS) with graphene oxide (GO) to produce composite elastomers. These materials undergo chemical crosslinking between secondary amides near PDMS chain ends and epoxies on the surface of GO as confirmed by infrared spectroscopy, rheology, gel content, and mechanical property measurements. The incorporation of pyrene end groups introduces π–π interactions with GO surfaces that enhance the reaction efficacy of the nearby secondary amide groups. As a comparison, methoxy‐terminated telechelic PDMS containing the same secondary amides near the chain ends did not exhibit appreciable crosslinking with GO. Depending on the concentration of the amide groups, the pyrene‐terminated PDMS/GO elastomer can be highly crosslinked (e.g., up to 96 wt % gel) but highly extensible (e.g., extensional strains of more than 200%). This general strategy could be implemented using other amide containing polymers to produce a wide range of high‐performance thermosets and elastomers. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017, 55, 1406–1413

We report the synthesis and properties of a low-density (∼5 mg/cm³) and highly porous (99.6% void space) three-dimensional reduced graphene oxide (rGO)/poly(acrylic acid) (PAA) nanocomposite aerogel as the scaffold for cathode materials in lithium-ion batteries (LIBs). The rGO-PAA is both simple and starts from readily available graphite and PAA, thereby providing a scalable fabrication procedure. The scaffold can support as much as a 75 mg/cm² loading of LiFePO₄ (LFP) in a ∼430 μm thick layer, and the porosity of the aerogel is tunable by compression; the flexible aerogel can be compressed 30-fold (i.e., to as little as 3.3% of its initial volume) while retaining its mechanical integrity. Replacement of the Al foil by the rGO-PAA current collector of the slurry-cast LFP (1.45 ± 0.2 g/cm³ tap density) provides for exemplary mass loadings of 9 mg_LFP/cm² at 70 μm thickness and 1.4 g/cm³ density or 16 mg_LFP/cm² at 100 μm thickness and ∼1.6 g/cm³ density. When compared to Al foil, the distribution of LFP throughout the three-dimensional rGO-PAA framework doubles the effective LFP solution-contacted area at 9 mg/cm² loading and increases it 2.5-fold at 16 mg/cm² loading. Overall, the rGO-PAA current collector increases the volumetric capacity by increasing the effective electrode area without compromising the electrode density, which was compromised in past research where the effective electrode area has been increased by reducing the particle size.

Stretchable energy‐storage devices receive considerable attention due to their promising applications in future wearable technologies. However, they currently suffer from many problems, including low utility of active materials, limited multidirectional stretchability, and poor stability under stretched conditions. In addition, most proposed designs use one or more rigid components that fail to meet the stretchability requirement for the entire device. Here, an all‐stretchable‐component sodium‐ion full battery based on graphene‐modified poly(dimethylsiloxane) sponge electrodes and an elastic gel membrane is developed for the first time. The battery exhibits reasonable electrochemical performance and robust mechanical deformability; its electrochemical characteristics can be well‐maintained under many different stretched conditions and after hundreds of stretching–release cycles. This novel design integrating all stretchable components provides a pathway toward the next generation of wearable energy devices in modern electronics.