Courtney Ann Downes

Electrocatalytic systems based on metal–organic frameworks (MOFs) have attracted great attention due to their potential application in commercially viable renewable energy-converting devices. We have recently shown that the cobalt 2,3,6,7,10,11-triphenylenehexathiolate (CoTHT) framework can catalyze the hydrogen evolution reaction (HER) in fully aqueous media with Tafel slopes as low as 71 mV/dec and near-unity Faradaic efficiency (FE). Taking advantage of the high synthetic tunability of MOFs, here, we synthesize a series of iron and mixed iron/cobalt THT-based MOFs. The incorporation of the iron and cobalt dithiolene moieties is verified by various spectroscopic techniques, and the integrity of the crystalline structure is maintained regardless of the stoichiometries of the two metals. The hydrogen evolving activity of the materials was explored in pH 1.3 aqueous electrolyte solutions. Unlike CoTHT, the FeTHT framework exhibits minimal activity due to a late catalytic onset [−0.440 V versus reversible hydrogen electrode (RHE)] and a large Tafel slope (210 mV/dec). The performance of the mixed-metal MOFs is adversely affected by the incorporation of Fe, where increasing Fe content results in MOFs with lower HER activity and diminished long-term stability and FE for H₂ production. It is proposed that the FeTHT domains undergo alternative Faradaic processes under catalytic conditions, which alter its local structure and electrochemical behavior, eventually resulting in a material with diminished HER performance.

Despite the promising previous reports on the development of electrocatalytic dithiolene-based metal–organic frameworks (MOFs) for the hydrogen evolution reaction (HER), these materials often display poor reproducibility of the HER performance because of their poor bulk properties upon integration with electrode materials. We demonstrate here an in-depth investigation of the electrocatalytic HER activity of a cobalt 2,3,6,7,10,11-triphenylenehexathiolate (CoTHT) MOF. To enhance the durability and charge transport properties of the constructed CoTHT/electrode architecture, CoTHT is deposited as an ink composite (1) composed of Nafion and carbon black. We leverage here the well-established use of catalyst inks in the literature to increase adhesion of the catalyst to the electrode surface and to improve the overall electrical conductivity of the integrated catalyst/electrode. The utilization of the composite 1 leads to a significant improvement in the overpotential (η) to reach a current density of 10 mA/cm² (η = 143 mV) compared to prior reports, resulting in the most active MOF-based electrocatalyst for the HER that contains only earth-abundant elements. Extensive density functional theory (DFT) calculations were applied to understand the structure of CoTHT and the mechanistic pathways of the HER. The computational results suggest that an AB stacking geometry is energetically favorable, where one layer is slipped by 1.6 Å relative to the neighboring one along the a and b vectors. Additionally, the DFT calculations indicate that the catalytic cycle likely involves a Volmer discharge step to generate a cobalt hydride, followed by a Heyrovsky step to form a cobalt–H₂ intermediate, and finally the dissociation of H₂.

Metal-organic frameworks (MOFs) containing redox active linkers have led to hybrid compounds exhibiting high electrical conductivity, which enables their use in applications in electronics and electrocatalysis. While many computational studies predict two-dimensional (2D) MOFs to be metallic, the majority of experiments show decreasing conductivity on cooling, indicative of a gap in the electronic band structure. To date, only a handful of MOFs have been reported that exhibit increased electrical conductivity upon cooling indicative of a metallic character, which highlights the need for better understanding the origin of the conductivity. A 2D MOF containing iron bis(dithiolene) motifs was recently reported to exhibit semiconducting behavior with record carrier mobility. Herein, we report that high crystallinity and the elimination of guest species results in an iron 2,3,6,7,10,11-tripheylenehexathiolate (THT) MOF, FeTHT, exhibiting a complex transition from semiconducting to metallic upon cooling, similar to what was shown for the analogous CoTHT. Remarkably, exposing the FeTHT to air significantly influences the semiconducting-to-metallic transition temperature (100 to 300 K), and ultimately results in a material showing metallic-like character at, and above, room temperature. This study indicates these materials can tolerate a substantial degree of doping that ultimately results in charge delocalization and metallic-like conductivity, an important step towards enabling their use in chemiresistive sensing and optoelectronics.