Apostolos Baklavaridis

Purpose. Chromite samples from Aetoraches mine area in the southern part of the Vourinos complex in Western Macedonia, Greece were examined from mineralogical-geochemical perspective. Methods. Χ-ray Diffraction (XRD) mineral phase analysis, elemental Scanning Electron Microscopy coupled with Energy Dispersive Spectroscopy (SEM-EDS) analysis and Thermogravimetry/Differential Thermogravimetry (TG/DTG) were carried out. Findings. The XRD results showed that all the samples contain mainly magnesium- and aluminum-chromite (“aluminum-picrochromite”) phases, along with forsterite (magnesian olivine), serpentine and chlorite occurrences. Based on the SEM-EDS results, the computed average chemical formula indicative of this specific chromite type is: (Fe0.4 Mg0.6) (Cr1.6 Al0.4/)O4. The TG-DTG weight losses found to be in the range of 4.4-14.36%, at temperatures between 600 and 750°C, indicated the presence of the hydroxyl-rich silicate minerals, serpentinite and chlorite, in agreement to the Loss of Ignition (LOI) results. The mineral phases detected in the present analyses appear in the dunite/diorite/harzburgite/peridotite main rocks of the ophiolitic complex that hosts the chromite ore. Originality.In the current research, an original characterization, via thorough elemental, phase and thermal analysis, is carried out aiming to enlighten the geochemistry aspects of the Vourinos chromite complex, Region of Western Macedonia, Greece, particularly of easily accessible and exploitable chromite deposits of the Aetoraches mine area. Practical implications. The chromite mineral, and especially the metallurgical type, is of substantial importance in metal industry. In that sense, the findings of the present investigation of chromite purity and mineral structure is a prerequisite for future exploitation of the Aetoraches chromite deposits in particular and broadly for the ongoing exploitation of chromite ore in the Vourinos complex, situated in Region of Western Macedonia, Greece, an area with high unemployment and rather slow economic growth. Keywords: chromite ore, Vourinos massif, Aetoraches mine area, mineralogical characterization, geochemistry, XRD, SEM-EDS, TG/DTG

The current study presents an original chemical, elemental and mineralogical characterization of new quartz mineral deposits situated in Ios island, Cyclades, Aegean sea, Greece, via X-Ray Diffraction (XRD), Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM-EDS) and Inductively Coupled Plasma Mass Spectrometry (ICP-MS) trace-element analysis. Actually, the mineral Quartz (crystalline SiO2) is found in nature in varying quality and is explored and traded for use in different applications of significant importance depending on the quartz purity. The results of the thorough chemical and mineralogical analysis indicate that quartz originating from the location examined in this research is almost free from other microcrystalline phases, and therefore it can be characterized as highly pure α-quartz. Thus, it can be used in the industry of ultra-high purity quartz production for specific applications, as long as the deposits are exploitable. In this framework, a preliminary estimation of the economic benefits from a potential exploration versus the environmental aspects of mining, taking into account sustainability issues in the region, is provided highlighting the local social needs

The time-on-stream catalytic performance and stability of 8 wt. % Ni catalyst supported on two commercially available catalytic supports, ZrO₂ and 15 wt.% WO₃-ZrO₂, was investigated under the biogas dry reforming reaction for syngas production, at 750°C and a biogas quality equal to CH₄/CO₂ = 1.5, that represents a common concentration of real biogas. A number of analytical techniques such as N₂ adsorption/desorption (BET method), XRD, H₂-TPR, NH₃- and CO₂-TPD, SEM, ICP, thermal analysis (TGA/DTG) and Raman spectroscopy were used in order to determine textural, structural and other physicochemical properties of the catalytic materials, and the type of carbon deposited on the catalytic surface of spent samples. These techniques were used in an attempt to understand better the effects of WO₃-induced modifications on the catalyst morphology, physicochemical properties and catalytic performance. Although Ni dispersion and reducibility characteristics were found superior on the modified Ni/WZr sample than that on Ni/Zr, its dry reforming of methane (DRM) performance was inferior; a result attributed to the enhanced acidity and complete loss of the basicity recorded on this catalyst, an effect that competes and finally overshadows the benefits of the other superior properties. Raman studies revealed that the degree of graphitization decreases with the insertion of WO₃ in the crystalline structure of the ZrO₂ support, as the I_D/I_G peak intensity ratio is 1.03 for the Ni/Zr and 1.29 for the Ni/WZr catalyst.

Chitosan nanofibers reinforced with tungsten disulfide inorganic nanotubes (INT-WS₂) were fabricated in this study. The aim was to investigate the effect of the material parameters and the electrospinning process parameters on the obtained nanofibrous morphology of the mats. The INT-WS₂ content, the polymer solution concentration, the electric field strength, and the solution's flow rate were the investigated factors within the framework of response surface methodology. Scanning electron microscopic and image analysis were used for the dimensional characterization of the nanofibrous morphology and the estimation of three selected responses. Two responses were related to the quality of the nanofibrous morphology: the number surface density of the beads ( N_bead) and the average bead-to-fiber diameter ( D_bead/ D_fiber). The third response was indicative of the fiber thickness ( D_fiber). The developed models as well as the coupling and the individual effects of the four investigated factors are given. The results indicate that the electrospun nanofibrous morphology is mostly affected by the polymer solution concentration, the electric field strength and the INT-WS₂ loading. Furthermore, the response-surface results reveal possible experimental pathways that may be followed in order to obtain specified nanofibrous chitosan/INT-WS₂ morphologies.

The development of value-added ceramic materials deriving only from industrial by-products is particularly interesting from technological, economic, and environmental point of views. In this work, the synergistic sintering of ternary and binary mixtures of fly ash, steelmaking electric arc furnace dust, and ladle furnace slag for the synthesis of compacted ceramics is reported. The sintered specimens’ microstructure and mineralogical composition were characterized by SEM-EDS and XRD, respectively. Moreover, the shrinkage, apparent density, water absorption, and Vickers microhardness (HV) were investigated at different sintering temperatures and raw material compositions. The characterization of the sintered compacts revealed the successful consolidation of the ceramic microstructures. According to the experimental findings, the ceramics obtained from fly ash/steel dust mixtures exhibited enhanced properties compared to the other mixtures tested. Moreover, the processing temperature affected the final properties of the produced ceramics. Specifically, a 407% HV increase for EAFD and a 2221% increase for the FA-EAFD mixture were recorded, by increasing the sintering temperature from 1050 to 1150°C. Likewise, a 972% shrinkage increase for EAFD and a 577% shrinkage increase for the FA-EAFD mixture were recorded, by increasing the sintering temperature from 1050 to 1150°C. The research results aim at shedding more light on the development of sustainable sintered ceramics from secondary industrial resources towards circular economy.