Takaaki Koyanagi

This report documents the design of a High Flux Isotope Reactor (HFIR) irradiation experiment intended to evaluate irradiation effects on the hermeticity of silicon carbide (SiC) end plug specimens under a radial fast neutron flux gradient at representative light-water reactor (LWR) temperatures of approximately 300 °C. The overarching goal of this work is to statistically evaluate SiC end plug hermeticity and mechanical properties following irradiation using the high-throughput irradiation capability discussed here. Each specimen consists of a short section of SiC fiber–reinforced SiC (SiC/SiC) tube with a single monolithic SiC end plug joined to one end. The experiment allows up to 66 specimens to be irradiated in six different stacks within a dry, sealed irradiation capsule derived from the previously developed high-temperature SiC/SiC cladding bowing experiment. The neutronics basis, thermal analysis, and HFIR readiness of the experiment are discussed in this report for two possible design cases. The first design case is based on existing approval documentation and components that are on hand and approved for use, so the experiment insertion would require only specimen receipt, specimen pre-irradiation characterization, experiment assembly, and final fabrication package approval. The second design case provides improved thermal robustness and the preferred end plug geometry but requires fabrication of a modified holder and revisions to the HFIR approval documentation, in addition to the other activities required for the first design case, before insertion.

This report presents a workflow for advancing fuel performance modeling of SiC composite cladding for light-water reactors by linking microscale, experimental data-informed finite element analysis with rod-scale fuel performance codes such as BISON. The workflow uses X-ray computed tomography (XCT) to capture the actual geometry and processing-induced defects of as-fabricated SiC composite tube specimens, particularly porosity and wall-thickness variations, and converts the segmented XCT volumes into image-based finite element meshes for high fidelity structural analysis.

A framework for the mapping and quantification of geometrical discrepancies in additively manufactured ceramics is described with a focus on 3D-printed SiC objects, manufactured via binder jet additive manufacturing (BJAM) followed by densification with chemical vapor infiltration. X-ray computed tomography with deep-learning-aided segmentation that employs a 2.5D U-Net architecture was used to investigate site-specific geometrical discrepancies between CAD and 3D-printed parts, and their quantification. For complex geometries, analysis revealed that a highly anisotropic discrepancy distribution occurs that requires detailed subcomponent-based investigation. An effective design feedback mechanism stemming from such a framework is necessary to accommodate process tuning aimed at specific discrepancies. Areas that challenged the BJAM process required defining realistic acceptable tolerance levels for industrial applications.

The SiC-based materials, particularly SiC-fiber-reinforced SiC matrix (SiC/SiC) composites, show strong potential for structural and functional applications in future fusion power plants because they can operate at high temperatures with a range of coolants and breeders, thereby enabling higher energy conversion efficiency. This paper presents recent advancements in the development of SiC-based materials, focusing on processing techniques and material performance and resistance under fusion-relevant environments. The processing activities have emphasized near-net-shape fabrication and the joining of SiC subcomponents, with processing methods and material compositions informed by previous irradiation experiments on various grades of SiC. Research on irradiation effects has remained focused on degradation mechanisms and the microstructural optimization of SiC/SiC composites irradiated to high neutron damage levels. Analysis of irradiation defects in SiC has advanced via the application of cutting-edge characterization methods, among which Raman spectroscopy is becoming a common tool to assess atomic-scale chemical disorder. Fusion–fission crosscutting irradiation research has explored combined effects in SiC/SiC composites with application-relevant geometries, including bowing of SiC/SiC composite channels under neutron flux gradients, stress evolution in SiC/SiC composite tubes under through-thickness temperature gradients, and irradiation-enhanced corrosion in SiC. Finally, research opportunities for component testing and assessment under fusion-relevant conditions, in support of emerging concepts from the private fusion sector, are discussed.

The neutron dose-dependent evolutions and the underlying mechanisms of properties of SiC fiber-reinforced SiC matrix (SiC/SiC) composites at a temperature relevant to light-water reactors (~600 K) were investigated and analyzed. Chemical vapor infiltrated (CVI) SiC/SiC composites reinforced with Hi-Nicalon Type S or Tyranno SA3 fiber were neutron-irradiated to doses up to 30 dpa. The irradiated composites retained their flexural strengths. The thermal diffusivity and dimensional changes were mostly retained from 2.0 to 30.2 dpa. Discrepancies in irradiation responses among CVI SiC/SiC composites from different sources were found. Additional microstructural analysis using Raman spectroscopy and numerical analysis on irradiation effect on residual stress were used to explain how the microstructural variables, especially of carbon interphases, affect the mechanical properties in the 30–40 dpa dose range.

Traditional CVI process optimization involves many lengthy experiments directly on CVI equipment. Here, a workflow combining CALPHAD thermodynamics and experimental CVD is used to rapidly optimize CVI SiC growth – avoiding pitfalls in parameters.