Nadejda Horchidan

BaTiO₃ (BTO) nanoparticles produced by wet chemistry methods were embedded in several types of flexible materials in order to fabricate flexible electronic devices. Starting from the produced nanoparticle dielectric properties, flexible material dielectric properties were tested for high electromagnetic frequencies (30 GHz–2 THz) using time domain spectroscopy. Dielectric performances of the different materials obtained with variable nanoparticle concentrations up to 40 wt.%, embedded in, gelatin, epoxy, and styrene-butadiene were compared at several working temperatures between 0 °C and 120 °C. Beside the general trend of ε′ decrease with temperature and loses increase with the operating frequency, we were able to identify few matrix dependent optimal nanoparticle concentrations. The best composite performances were achieved by the BTO-SBS matrix, with filler concentration of 2 wt.%, where the losses have been of 1.5%, followed by BTO-gelatin matrix, with filler concentration of 40 wt.%, with higher losses percent of almost 10% for THz frequencies.

The paper presents a study concerning the role of ferroelectric filler size and clustering in the dielectric properties of 20%BaTiO₃-80%PVDF and of 20% (2%Ag-98%BaTiO₃)-PVDF hybrid nanocomposites. By finite element calculations, it was shown that using fillers with ε > 10³ does not provide a permittivity rise in the composites and the effective dielectric constant tends to saturate to specific values determined by the filler size and agglomeration degree. Irrespective of the ferroelectric filler sizes, the addition of metallic ultrafine nanoparticles (Ag) results in permittivity intensification and the effect is even stronger if the metallic nanoparticles are connected to a higher degree with the ferroelectric particles' surfaces. When using coarse ferroelectric fillers, the probability of clustering is higher, thus favoring the permittivity increase by field concentration in small regions close to the interfaces separating dissimilar materials. The modeling results were validated by an experimental dielectric analysis performed in a series of PVDF-based thick films with the same amount of BaTiO₃ fillers or with Ag-BaTiO₃ hybrid fillers. Similar trends as predicted by simulations were found experimentally but with slightly higher permittivity values which were assigned to the modifications of the polymer phase composition due to the presence of nanofillers and the local sample inhomogeneity (the presence of clustering, in particular for coarse BaTiO₃ grains), which create regions with enhanced local fields.

Lead-free piezoelectric ceramics with nominal composition at morphotropic phase boundary Ba_0.85Ca_0.15Ti_0.9Zr_0.1O₃ (BCTZ) prepared by different processing routes and sintered either by conventional solid-state reaction or by spark plasma sintering (SPS) techniques were comparatively investigated to observe the role of structural modifications and of microstructures on the dielectric, ferroelectric, piezoelectric and electrocaloric responses. The ceramics presented relative densities from 75% to 97% and showed variations in their phase composition as a result of variable mixing and different synthesis and sintering parameters providing local compositional heterogeneity. As result, all of the ceramics showed diffuse phase transition and ferroelectric switching responses, with parameters affected mostly by density (P_r between 3.6 to 10.1 μC/cm²). High values for the electrocaloric response in the Curie range were found for the ceramics with predominantly orthorhombic character. Field-induced structural modifications were probed by tunability anomalies and by XRD experiments in remanence conditions. Piezoelectric effects with notably high figure of merit values were assigned to the better densification and poling efficiency of BCTZ ceramics.