Greyish-purple tremolite jade has become well known in the past few years, and the origin of its color has attracted the attention of gemologists. In this study, FT-IR spectra, EPMA, EPR spectra, micro-XRF, UV–Vis–NIR spectra, and LA-ICP-MS in situ mapping were analyzed to investigate the chromophore elements. The study sample was chosen from the Sanchahe mine, Qinghai Province, NW China, which has the typical characteristics of a gradual color change. The FT-IR and EPMA results revealed that the mineral composition of the dark and light greyish-purple regions of the sample are primarily composed of tremolite. UV–Vis–NIR spectra demonstrated that the greyish-purple color is mainly due to strong absorptions at 560 nm and 700 nm and weak absorption at 745 nm in the visible range. The EPR spectra presented ~3400 G six hyperfine lines resulting from the hyperfine interactions of the unpaired electron with the Mn²⁺ nucleus in the octahedral site. The UV–Vis–NIR and EPR spectra analyses demonstrated that Mn²⁺ is the origin of the purple color. A comparison of the major elements in the light and dark regions indicated that the chromogenic elements have strong positive correlations with Mn, Cu, and Fe. LA-ICP-MS mapping used to analyze the first transition metals indicated possible positive correlations between the greyish-purple color and the trace chromogenic elements. This suggested that the Mn, Cu, and Fe contents are significantly high in the dark band region. Combining in situ LA-ICP-MS mapping of trace elements, UV–Vis spectra, and EPR analysis results, it was suggested that Mn, Cu, and Fe are the major contributors to the greyish-purple color. This study provides a reference for the specific experimental methods to determine chromophores and the origin of color in tremolite jades.

In recent years, some sapphires were found to fade in sunlight and to increase their color after UV irradiation. This unstable color phenomenon is attributed to the photochromism of corundum. The photochromic effect seriously affects the grading and evaluation of sapphires, although its mechanism is still uncertain. Here, we performed a set of photochromic experiments on sapphire specimens using a 254 nm shortwave UV light source and a D65 light source (which simulates sunlight) to generate different color states exhibiting characteristic absorption, emission, and excitation spectra. We observed that, for different color states, variation in the intensity of the absorption band at ~460 nm was consistent with that of orange fluorescence at 500–800 nm. This observation indicates a relationship between color instability and orange fluorescence. Peaks in excitation spectra at 320, 420, 490, 560, and 637 nm provide insight into the source(s) of excited orange fluorescence, which are related to different types of F-centers and Mg-trapped holes. We propose an explanation for the photochromic phenomenon: the color of photochromic yellow sapphire is the result of a variety of defects that release orange fluorescence simultaneously. Further, we hypothesize that the mechanism of photochromism in yellow sapphires is linked to electron transfer between F-centers and Mg-trapped holes.